R31538 Cobalt vs. EN 1.4762 Stainless Steel

R31538 cobalt belongs to the cobalt alloys classification, while EN 1.4762 stainless steel belongs to the iron alloys. They have a modest 26% of their average alloy composition in common, which, by itself, doesn't mean much. There are 27 material properties with values for both materials. Properties with values for just one material (8, in this case) are not shown.

For each property being compared, the top bar is R31538 cobalt and the bottom bar is EN 1.4762 stainless steel.

Metric UnitsUS Customary Units

Mechanical Properties

Elastic (Young's, Tensile) Modulus, GPa 220
200
Elongation at Break, % 13 to 23
13
Fatigue Strength, MPa 310 to 480
180
Poisson's Ratio 0.29
0.27
Shear Modulus, GPa 86
78
Tensile Strength: Ultimate (UTS), MPa 1020 to 1360
620
Tensile Strength: Yield (Proof), MPa 580 to 930
310

Thermal Properties

Latent Heat of Fusion, J/g 320
300
Melting Completion (Liquidus), °C 1360
1410
Melting Onset (Solidus), °C 1290
1370
Specific Heat Capacity, J/kg-K 450
490
Thermal Conductivity, W/m-K 13
17
Thermal Expansion, µm/m-K 13
10

Electrical Properties

Electrical Conductivity: Equal Volume, % IACS 2.0
1.6
Electrical Conductivity: Equal Weight (Specific), % IACS 2.1
1.9

Otherwise Unclassified Properties

Density, g/cm3 8.4
7.6
Embodied Carbon, kg CO2/kg material 8.1
2.5
Embodied Energy, MJ/kg 110
37
Embodied Water, L/kg 530
170

Common Calculations

Resilience: Ultimate (Unit Rupture Work), MJ/m3 140 to 200
67
Resilience: Unit (Modulus of Resilience), kJ/m3 750 to 1920
250
Stiffness to Weight: Axial, points 15
15
Stiffness to Weight: Bending, points 24
26
Strength to Weight: Axial, points 34 to 45
23
Strength to Weight: Bending, points 27 to 32
21
Thermal Diffusivity, mm2/s 3.5
4.6
Thermal Shock Resistance, points 25 to 33
22

Alloy Composition

Aluminum (Al), % 0
1.2 to 1.7
Carbon (C), % 0.15 to 0.35
0 to 0.12
Chromium (Cr), % 26 to 30
23 to 26
Cobalt (Co), % 58.7 to 68.9
0
Iron (Fe), % 0 to 0.75
69.7 to 75.1
Manganese (Mn), % 0 to 1.0
0 to 1.0
Molybdenum (Mo), % 5.0 to 7.0
0
Nickel (Ni), % 0 to 1.0
0
Nitrogen (N), % 0 to 0.25
0
Phosphorus (P), % 0
0 to 0.040
Silicon (Si), % 0 to 1.0
0.7 to 1.4
Sulfur (S), % 0
0 to 0.015