R31538 Cobalt vs. EN 1.7219 Steel

R31538 cobalt belongs to the cobalt alloys classification, while EN 1.7219 steel belongs to the iron alloys. There are 27 material properties with values for both materials. Properties with values for just one material (7, in this case) are not shown.

For each property being compared, the top bar is R31538 cobalt and the bottom bar is EN 1.7219 steel.

Metric UnitsUS Customary Units

Mechanical Properties

Elastic (Young's, Tensile) Modulus, GPa 220
190
Elongation at Break, % 13 to 23
19
Fatigue Strength, MPa 310 to 480
340
Poisson's Ratio 0.29
0.29
Shear Modulus, GPa 86
73
Tensile Strength: Ultimate (UTS), MPa 1020 to 1360
650
Tensile Strength: Yield (Proof), MPa 580 to 930
490

Thermal Properties

Latent Heat of Fusion, J/g 320
250
Melting Completion (Liquidus), °C 1360
1460
Melting Onset (Solidus), °C 1290
1420
Specific Heat Capacity, J/kg-K 450
470
Thermal Conductivity, W/m-K 13
44
Thermal Expansion, µm/m-K 13
13

Electrical Properties

Electrical Conductivity: Equal Volume, % IACS 2.0
7.3
Electrical Conductivity: Equal Weight (Specific), % IACS 2.1
8.4

Otherwise Unclassified Properties

Density, g/cm3 8.4
7.8
Embodied Carbon, kg CO2/kg material 8.1
1.5
Embodied Energy, MJ/kg 110
20
Embodied Water, L/kg 530
51

Common Calculations

Resilience: Ultimate (Unit Rupture Work), MJ/m3 140 to 200
110
Resilience: Unit (Modulus of Resilience), kJ/m3 750 to 1920
650
Stiffness to Weight: Axial, points 15
13
Stiffness to Weight: Bending, points 24
24
Strength to Weight: Axial, points 34 to 45
23
Strength to Weight: Bending, points 27 to 32
21
Thermal Diffusivity, mm2/s 3.5
12
Thermal Shock Resistance, points 25 to 33
19

Alloy Composition

Carbon (C), % 0.15 to 0.35
0.22 to 0.29
Chromium (Cr), % 26 to 30
0.9 to 1.2
Cobalt (Co), % 58.7 to 68.9
0
Copper (Cu), % 0
0 to 0.3
Iron (Fe), % 0 to 0.75
96.7 to 98.2
Manganese (Mn), % 0 to 1.0
0.5 to 0.8
Molybdenum (Mo), % 5.0 to 7.0
0.15 to 0.3
Nickel (Ni), % 0 to 1.0
0
Nitrogen (N), % 0 to 0.25
0
Phosphorus (P), % 0
0 to 0.025
Silicon (Si), % 0 to 1.0
0 to 0.35
Sulfur (S), % 0
0 to 0.010