R31538 Cobalt vs. CC499K Bronze

R31538 cobalt belongs to the cobalt alloys classification, while CC499K bronze belongs to the copper alloys. There are 26 material properties with values for both materials. Properties with values for just one material (6, in this case) are not shown.

For each property being compared, the top bar is R31538 cobalt and the bottom bar is CC499K bronze.

Metric UnitsUS Customary Units

Mechanical Properties

Elastic (Young's, Tensile) Modulus, GPa 220
110
Elongation at Break, % 13 to 23
13
Poisson's Ratio 0.29
0.34
Shear Modulus, GPa 86
41
Tensile Strength: Ultimate (UTS), MPa 1020 to 1360
260
Tensile Strength: Yield (Proof), MPa 580 to 930
120

Thermal Properties

Latent Heat of Fusion, J/g 320
190
Melting Completion (Liquidus), °C 1360
1000
Melting Onset (Solidus), °C 1290
920
Specific Heat Capacity, J/kg-K 450
370
Thermal Conductivity, W/m-K 13
73
Thermal Expansion, µm/m-K 13
18

Electrical Properties

Electrical Conductivity: Equal Volume, % IACS 2.0
12
Electrical Conductivity: Equal Weight (Specific), % IACS 2.1
12

Otherwise Unclassified Properties

Density, g/cm3 8.4
8.8
Embodied Carbon, kg CO2/kg material 8.1
3.1
Embodied Energy, MJ/kg 110
51
Embodied Water, L/kg 530
350

Common Calculations

Resilience: Ultimate (Unit Rupture Work), MJ/m3 140 to 200
27
Resilience: Unit (Modulus of Resilience), kJ/m3 750 to 1920
65
Stiffness to Weight: Axial, points 15
6.9
Stiffness to Weight: Bending, points 24
18
Strength to Weight: Axial, points 34 to 45
8.1
Strength to Weight: Bending, points 27 to 32
10
Thermal Diffusivity, mm2/s 3.5
22
Thermal Shock Resistance, points 25 to 33
9.2

Alloy Composition

Aluminum (Al), % 0
0 to 0.010
Antimony (Sb), % 0
0 to 0.1
Arsenic (As), % 0
0 to 0.030
Bismuth (Bi), % 0
0 to 0.020
Cadmium (Cd), % 0
0 to 0.020
Carbon (C), % 0.15 to 0.35
0
Chromium (Cr), % 26 to 30
0 to 0.020
Cobalt (Co), % 58.7 to 68.9
0
Copper (Cu), % 0
84 to 88
Iron (Fe), % 0 to 0.75
0 to 0.3
Lead (Pb), % 0
0 to 3.0
Manganese (Mn), % 0 to 1.0
0
Molybdenum (Mo), % 5.0 to 7.0
0
Nickel (Ni), % 0 to 1.0
0 to 0.6
Nitrogen (N), % 0 to 0.25
0
Phosphorus (P), % 0
0 to 0.040
Silicon (Si), % 0 to 1.0
0 to 0.010
Sulfur (S), % 0
0 to 0.040
Tin (Sn), % 0
4.0 to 6.0
Zinc (Zn), % 0
4.0 to 6.0