R31538 Cobalt vs. CC755S Brass

R31538 cobalt belongs to the cobalt alloys classification, while CC755S brass belongs to the copper alloys. There are 26 material properties with values for both materials. Properties with values for just one material (6, in this case) are not shown.

For each property being compared, the top bar is R31538 cobalt and the bottom bar is CC755S brass.

Metric UnitsUS Customary Units

Mechanical Properties

Elastic (Young's, Tensile) Modulus, GPa 220
100
Elongation at Break, % 13 to 23
9.5
Poisson's Ratio 0.29
0.31
Shear Modulus, GPa 86
40
Tensile Strength: Ultimate (UTS), MPa 1020 to 1360
390
Tensile Strength: Yield (Proof), MPa 580 to 930
250

Thermal Properties

Latent Heat of Fusion, J/g 320
170
Melting Completion (Liquidus), °C 1360
820
Melting Onset (Solidus), °C 1290
780
Specific Heat Capacity, J/kg-K 450
390
Thermal Conductivity, W/m-K 13
120
Thermal Expansion, µm/m-K 13
21

Electrical Properties

Electrical Conductivity: Equal Volume, % IACS 2.0
27
Electrical Conductivity: Equal Weight (Specific), % IACS 2.1
30

Otherwise Unclassified Properties

Density, g/cm3 8.4
8.1
Embodied Carbon, kg CO2/kg material 8.1
2.7
Embodied Energy, MJ/kg 110
46
Embodied Water, L/kg 530
330

Common Calculations

Resilience: Ultimate (Unit Rupture Work), MJ/m3 140 to 200
33
Resilience: Unit (Modulus of Resilience), kJ/m3 750 to 1920
290
Stiffness to Weight: Axial, points 15
7.1
Stiffness to Weight: Bending, points 24
19
Strength to Weight: Axial, points 34 to 45
14
Strength to Weight: Bending, points 27 to 32
15
Thermal Diffusivity, mm2/s 3.5
38
Thermal Shock Resistance, points 25 to 33
13

Alloy Composition

Aluminum (Al), % 0
0.4 to 0.7
Carbon (C), % 0.15 to 0.35
0
Chromium (Cr), % 26 to 30
0
Cobalt (Co), % 58.7 to 68.9
0
Copper (Cu), % 0
59.5 to 61
Iron (Fe), % 0 to 0.75
0.050 to 0.2
Lead (Pb), % 0
1.2 to 1.7
Manganese (Mn), % 0 to 1.0
0 to 0.050
Molybdenum (Mo), % 5.0 to 7.0
0
Nickel (Ni), % 0 to 1.0
0 to 0.2
Nitrogen (N), % 0 to 0.25
0
Silicon (Si), % 0 to 1.0
0 to 0.050
Tin (Sn), % 0
0 to 0.3
Zinc (Zn), % 0
35.8 to 38.9