R31538 Cobalt vs. CC766S Brass

R31538 cobalt belongs to the cobalt alloys classification, while CC766S brass belongs to the copper alloys. There are 26 material properties with values for both materials. Properties with values for just one material (6, in this case) are not shown.

For each property being compared, the top bar is R31538 cobalt and the bottom bar is CC766S brass.

Metric UnitsUS Customary Units

Mechanical Properties

Elastic (Young's, Tensile) Modulus, GPa 220
110
Elongation at Break, % 13 to 23
28
Poisson's Ratio 0.29
0.31
Shear Modulus, GPa 86
40
Tensile Strength: Ultimate (UTS), MPa 1020 to 1360
500
Tensile Strength: Yield (Proof), MPa 580 to 930
190

Thermal Properties

Latent Heat of Fusion, J/g 320
180
Melting Completion (Liquidus), °C 1360
840
Melting Onset (Solidus), °C 1290
800
Specific Heat Capacity, J/kg-K 450
390
Thermal Conductivity, W/m-K 13
89
Thermal Expansion, µm/m-K 13
20

Electrical Properties

Electrical Conductivity: Equal Volume, % IACS 2.0
32
Electrical Conductivity: Equal Weight (Specific), % IACS 2.1
36

Otherwise Unclassified Properties

Density, g/cm3 8.4
8.0
Embodied Carbon, kg CO2/kg material 8.1
2.8
Embodied Energy, MJ/kg 110
48
Embodied Water, L/kg 530
330

Common Calculations

Resilience: Ultimate (Unit Rupture Work), MJ/m3 140 to 200
110
Resilience: Unit (Modulus of Resilience), kJ/m3 750 to 1920
180
Stiffness to Weight: Axial, points 15
7.3
Stiffness to Weight: Bending, points 24
20
Strength to Weight: Axial, points 34 to 45
17
Strength to Weight: Bending, points 27 to 32
18
Thermal Diffusivity, mm2/s 3.5
28
Thermal Shock Resistance, points 25 to 33
17

Alloy Composition

Aluminum (Al), % 0
0.3 to 1.8
Antimony (Sb), % 0
0 to 0.1
Carbon (C), % 0.15 to 0.35
0
Chromium (Cr), % 26 to 30
0
Cobalt (Co), % 58.7 to 68.9
0
Copper (Cu), % 0
58 to 64
Iron (Fe), % 0 to 0.75
0 to 0.5
Lead (Pb), % 0
0 to 0.5
Manganese (Mn), % 0 to 1.0
0 to 0.5
Molybdenum (Mo), % 5.0 to 7.0
0
Nickel (Ni), % 0 to 1.0
0 to 2.0
Nitrogen (N), % 0 to 0.25
0
Silicon (Si), % 0 to 1.0
0 to 0.6
Tin (Sn), % 0
0 to 0.5
Zinc (Zn), % 0
29.5 to 41.7