R31538 Cobalt vs. SAE-AISI 4028 Steel

R31538 cobalt belongs to the cobalt alloys classification, while SAE-AISI 4028 steel belongs to the iron alloys. There are 27 material properties with values for both materials. Properties with values for just one material (6, in this case) are not shown.

For each property being compared, the top bar is R31538 cobalt and the bottom bar is SAE-AISI 4028 steel.

Metric UnitsUS Customary Units

Mechanical Properties

Elastic (Young's, Tensile) Modulus, GPa 220
190
Elongation at Break, % 13 to 23
14 to 23
Fatigue Strength, MPa 310 to 480
180 to 330
Poisson's Ratio 0.29
0.29
Shear Modulus, GPa 86
73
Tensile Strength: Ultimate (UTS), MPa 1020 to 1360
490 to 630
Tensile Strength: Yield (Proof), MPa 580 to 930
260 to 520

Thermal Properties

Latent Heat of Fusion, J/g 320
250
Melting Completion (Liquidus), °C 1360
1460
Melting Onset (Solidus), °C 1290
1420
Specific Heat Capacity, J/kg-K 450
470
Thermal Conductivity, W/m-K 13
49
Thermal Expansion, µm/m-K 13
12

Electrical Properties

Electrical Conductivity: Equal Volume, % IACS 2.0
7.1
Electrical Conductivity: Equal Weight (Specific), % IACS 2.1
8.1

Otherwise Unclassified Properties

Density, g/cm3 8.4
7.8
Embodied Carbon, kg CO2/kg material 8.1
1.5
Embodied Energy, MJ/kg 110
19
Embodied Water, L/kg 530
47

Common Calculations

Resilience: Ultimate (Unit Rupture Work), MJ/m3 140 to 200
81 to 95
Resilience: Unit (Modulus of Resilience), kJ/m3 750 to 1920
180 to 720
Stiffness to Weight: Axial, points 15
13
Stiffness to Weight: Bending, points 24
24
Strength to Weight: Axial, points 34 to 45
17 to 22
Strength to Weight: Bending, points 27 to 32
18 to 21
Thermal Diffusivity, mm2/s 3.5
13
Thermal Shock Resistance, points 25 to 33
16 to 20

Alloy Composition

Carbon (C), % 0.15 to 0.35
0.25 to 0.3
Chromium (Cr), % 26 to 30
0
Cobalt (Co), % 58.7 to 68.9
0
Iron (Fe), % 0 to 0.75
98.1 to 98.7
Manganese (Mn), % 0 to 1.0
0.7 to 0.9
Molybdenum (Mo), % 5.0 to 7.0
0.2 to 0.3
Nickel (Ni), % 0 to 1.0
0
Nitrogen (N), % 0 to 0.25
0
Phosphorus (P), % 0
0 to 0.035
Silicon (Si), % 0 to 1.0
0.15 to 0.35
Sulfur (S), % 0
0.035 to 0.050

Comparable Variants