R31538 Cobalt vs. SAE-AISI 52100 Steel

R31538 cobalt belongs to the cobalt alloys classification, while SAE-AISI 52100 steel belongs to the iron alloys. There are 27 material properties with values for both materials. Properties with values for just one material (6, in this case) are not shown.

For each property being compared, the top bar is R31538 cobalt and the bottom bar is SAE-AISI 52100 steel.

Metric UnitsUS Customary Units

Mechanical Properties

Elastic (Young's, Tensile) Modulus, GPa 220
190
Elongation at Break, % 13 to 23
10 to 20
Fatigue Strength, MPa 310 to 480
250 to 340
Poisson's Ratio 0.29
0.29
Shear Modulus, GPa 86
72
Tensile Strength: Ultimate (UTS), MPa 1020 to 1360
590 to 2010
Tensile Strength: Yield (Proof), MPa 580 to 930
360 to 560

Thermal Properties

Latent Heat of Fusion, J/g 320
250
Melting Completion (Liquidus), °C 1360
1450
Melting Onset (Solidus), °C 1290
1410
Specific Heat Capacity, J/kg-K 450
470
Thermal Conductivity, W/m-K 13
47
Thermal Expansion, µm/m-K 13
12 to 13

Electrical Properties

Electrical Conductivity: Equal Volume, % IACS 2.0
7.3
Electrical Conductivity: Equal Weight (Specific), % IACS 2.1
8.5

Otherwise Unclassified Properties

Density, g/cm3 8.4
7.8
Embodied Carbon, kg CO2/kg material 8.1
1.5
Embodied Energy, MJ/kg 110
20
Embodied Water, L/kg 530
51

Common Calculations

Resilience: Ultimate (Unit Rupture Work), MJ/m3 140 to 200
54 to 310
Resilience: Unit (Modulus of Resilience), kJ/m3 750 to 1920
350 to 840
Stiffness to Weight: Axial, points 15
13
Stiffness to Weight: Bending, points 24
24
Strength to Weight: Axial, points 34 to 45
21 to 72
Strength to Weight: Bending, points 27 to 32
20 to 45
Thermal Diffusivity, mm2/s 3.5
13
Thermal Shock Resistance, points 25 to 33
19 to 61

Alloy Composition

Carbon (C), % 0.15 to 0.35
0.93 to 1.1
Chromium (Cr), % 26 to 30
1.4 to 1.6
Cobalt (Co), % 58.7 to 68.9
0
Iron (Fe), % 0 to 0.75
96.5 to 97.3
Manganese (Mn), % 0 to 1.0
0.25 to 0.45
Molybdenum (Mo), % 5.0 to 7.0
0
Nickel (Ni), % 0 to 1.0
0
Nitrogen (N), % 0 to 0.25
0
Phosphorus (P), % 0
0 to 0.025
Silicon (Si), % 0 to 1.0
0.15 to 0.35
Sulfur (S), % 0
0 to 0.015

Comparable Variants