R31538 Cobalt vs. SAE-AISI O6 Steel
R31538 cobalt belongs to the cobalt alloys classification, while SAE-AISI O6 steel belongs to the iron alloys. There are 22 material properties with values for both materials. Properties with values for just one material (8, in this case) are not shown.
For each property being compared, the top bar is R31538 cobalt and the bottom bar is SAE-AISI O6 steel.
Metric UnitsUS Customary Units
Mechanical Properties
| Elastic (Young's, Tensile) Modulus, GPa | 220 | |
| 180 |
| Poisson's Ratio | 0.29 | |
| 0.29 |
| Shear Modulus, GPa | 86 | |
| 71 |
| Tensile Strength: Ultimate (UTS), MPa | 1020 to 1360 | |
| 670 to 2070 |
Thermal Properties
| Latent Heat of Fusion, J/g | 320 | |
| 260 |
| Melting Completion (Liquidus), °C | 1360 | |
| 1430 |
| Melting Onset (Solidus), °C | 1290 | |
| 1390 |
| Specific Heat Capacity, J/kg-K | 450 | |
| 480 |
| Thermal Conductivity, W/m-K | 13 | |
| 43 |
| Thermal Expansion, µm/m-K | 13 | |
| 12 |
Electrical Properties
| Electrical Conductivity: Equal Volume, % IACS | 2.0 | |
| 7.4 |
| Electrical Conductivity: Equal Weight (Specific), % IACS | 2.1 | |
| 8.6 |
Otherwise Unclassified Properties
| Density, g/cm3 | 8.4 | |
| 7.7 |
| Embodied Carbon, kg CO2/kg material | 8.1 | |
| 1.5 |
| Embodied Energy, MJ/kg | 110 | |
| 21 |
| Embodied Water, L/kg | 530 | |
| 47 |
Common Calculations
| Stiffness to Weight: Axial, points | 15 | |
| 13 |
| Stiffness to Weight: Bending, points | 24 | |
| 25 |
| Strength to Weight: Axial, points | 34 to 45 | |
| 24 to 74 |
| Strength to Weight: Bending, points | 27 to 32 | |
| 22 to 47 |
| Thermal Diffusivity, mm2/s | 3.5 | |
| 12 |
| Thermal Shock Resistance, points | 25 to 33 | |
| 22 to 69 |
Alloy Composition
| Carbon (C), % | 0.15 to 0.35 | |
| 1.3 to 1.6 |
| Chromium (Cr), % | 26 to 30 | |
| 0 to 0.3 |
| Cobalt (Co), % | 58.7 to 68.9 | |
| 0 |
| Copper (Cu), % | 0 | |
| 0 to 0.25 |
| Iron (Fe), % | 0 to 0.75 | |
| 94.6 to 97.7 |
| Manganese (Mn), % | 0 to 1.0 | |
| 0.3 to 1.1 |
| Molybdenum (Mo), % | 5.0 to 7.0 | |
| 0.2 to 0.3 |
| Nickel (Ni), % | 0 to 1.0 | |
| 0 to 0.3 |
| Nitrogen (N), % | 0 to 0.25 | |
| 0 |
| Phosphorus (P), % | 0 | |
| 0 to 0.030 |
| Silicon (Si), % | 0 to 1.0 | |
| 0.55 to 1.5 |
| Sulfur (S), % | 0 | |
| 0 to 0.030 |