R31538 Cobalt vs. C47000 Brass

R31538 cobalt belongs to the cobalt alloys classification, while C47000 brass belongs to the copper alloys. There are 24 material properties with values for both materials. Properties with values for just one material (8, in this case) are not shown.

For each property being compared, the top bar is R31538 cobalt and the bottom bar is C47000 brass.

Metric UnitsUS Customary Units

Mechanical Properties

Elastic (Young's, Tensile) Modulus, GPa 220
100
Elongation at Break, % 13 to 23
36
Poisson's Ratio 0.29
0.3
Shear Modulus, GPa 86
40
Tensile Strength: Ultimate (UTS), MPa 1020 to 1360
380
Tensile Strength: Yield (Proof), MPa 580 to 930
150

Thermal Properties

Latent Heat of Fusion, J/g 320
170
Melting Completion (Liquidus), °C 1360
900
Melting Onset (Solidus), °C 1290
890
Specific Heat Capacity, J/kg-K 450
390
Thermal Conductivity, W/m-K 13
120
Thermal Expansion, µm/m-K 13
21

Otherwise Unclassified Properties

Density, g/cm3 8.4
8.0
Embodied Carbon, kg CO2/kg material 8.1
2.7
Embodied Energy, MJ/kg 110
47
Embodied Water, L/kg 530
330

Common Calculations

Resilience: Ultimate (Unit Rupture Work), MJ/m3 140 to 200
110
Resilience: Unit (Modulus of Resilience), kJ/m3 750 to 1920
100
Stiffness to Weight: Axial, points 15
7.2
Stiffness to Weight: Bending, points 24
20
Strength to Weight: Axial, points 34 to 45
13
Strength to Weight: Bending, points 27 to 32
15
Thermal Diffusivity, mm2/s 3.5
38
Thermal Shock Resistance, points 25 to 33
13

Alloy Composition


Deprecated: Automatic conversion of false to array is deprecated in /home/public/compare.php on line 460
Aluminum (Al), % 0
0 to 0.010
Carbon (C), % 0.15 to 0.35
0
Chromium (Cr), % 26 to 30
0
Cobalt (Co), % 58.7 to 68.9
0
Copper (Cu), % 0
57 to 61
Iron (Fe), % 0 to 0.75
0
Lead (Pb), % 0
0 to 0.050
Manganese (Mn), % 0 to 1.0
0
Molybdenum (Mo), % 5.0 to 7.0
0
Nickel (Ni), % 0 to 1.0
0
Nitrogen (N), % 0 to 0.25
0
Silicon (Si), % 0 to 1.0
0
Tin (Sn), % 0
0.25 to 1.0
Zinc (Zn), % 0
37.5 to 42.8
Residuals, % 0
0 to 0.4