MakeItFrom.com
Menu (ESC)

R31538 Cobalt vs. C69710 Brass

R31538 cobalt belongs to the cobalt alloys classification, while C69710 brass belongs to the copper alloys. There are 26 material properties with values for both materials. Properties with values for just one material (6, in this case) are not shown.

For each property being compared, the top bar is R31538 cobalt and the bottom bar is C69710 brass.

Metric UnitsUS Customary Units

Mechanical Properties

Elastic (Young's, Tensile) Modulus, GPa 220
110
Elongation at Break, % 13 to 23
25
Poisson's Ratio 0.29
0.32
Shear Modulus, GPa 86
41
Tensile Strength: Ultimate (UTS), MPa 1020 to 1360
470
Tensile Strength: Yield (Proof), MPa 580 to 930
230

Thermal Properties

Latent Heat of Fusion, J/g 320
240
Melting Completion (Liquidus), °C 1360
930
Melting Onset (Solidus), °C 1290
880
Specific Heat Capacity, J/kg-K 450
400
Thermal Conductivity, W/m-K 13
40
Thermal Expansion, µm/m-K 13
19

Electrical Properties

Electrical Conductivity: Equal Volume, % IACS 2.0
8.0
Electrical Conductivity: Equal Weight (Specific), % IACS 2.1
8.7

Otherwise Unclassified Properties

Density, g/cm3 8.4
8.3
Embodied Carbon, kg CO2/kg material 8.1
2.7
Embodied Energy, MJ/kg 110
44
Embodied Water, L/kg 530
310

Common Calculations

Resilience: Ultimate (Unit Rupture Work), MJ/m3 140 to 200
99
Resilience: Unit (Modulus of Resilience), kJ/m3 750 to 1920
250
Stiffness to Weight: Axial, points 15
7.3
Stiffness to Weight: Bending, points 24
19
Strength to Weight: Axial, points 34 to 45
16
Strength to Weight: Bending, points 27 to 32
16
Thermal Diffusivity, mm2/s 3.5
12
Thermal Shock Resistance, points 25 to 33
16

Alloy Composition


Deprecated: Automatic conversion of false to array is deprecated in /home/public/compare.php on line 460
Arsenic (As), % 0
0.030 to 0.060
Carbon (C), % 0.15 to 0.35
0
Chromium (Cr), % 26 to 30
0
Cobalt (Co), % 58.7 to 68.9
0
Copper (Cu), % 0
75 to 80
Iron (Fe), % 0 to 0.75
0 to 0.2
Lead (Pb), % 0
0.5 to 1.5
Manganese (Mn), % 0 to 1.0
0 to 0.4
Molybdenum (Mo), % 5.0 to 7.0
0
Nickel (Ni), % 0 to 1.0
0
Nitrogen (N), % 0 to 0.25
0
Silicon (Si), % 0 to 1.0
2.5 to 3.5
Zinc (Zn), % 0
13.8 to 22
Residuals, % 0
0 to 0.5