High-silica Glass vs. SiAlON
High-silica glass belongs to the glass and glass-ceramics classification, while SiAlON belongs to the non-oxide engineering ceramics. There are 8 material properties with values for both materials. Properties with values for just one material (19, in this case) are not shown.
For each property being compared, the top bar is high-silica glass and the bottom bar is SiAlON.
Metric UnitsUS Customary Units
Material Properties
| Density, g/cm3 | 2.4 | |
| 3.3 |
| Dielectric Strength (Breakdown Potential), kV/mm | 34 | |
| 8.3 |
| Elastic (Young's, Tensile) Modulus, GPa | 78 | |
| 290 |
| Electrical Resistivity Order of Magnitude, 10x Ω-m | 12 | |
| 14 |
| Flexural Strength, MPa | 34 | |
| 680 |
| Stiffness to Weight: Axial, points | 19 | |
| 50 |
| Stiffness to Weight: Bending, points | 61 | |
| 67 |
| Thermal Expansion, µm/m-K | 0.6 to 0.75 | |
| 3.6 |