Solder Alloy 104 vs. 50Cr-50Ni-Cb Alloy

Both solder alloy 104 and 50Cr-50Ni-Cb alloy are otherwise unclassified metals. Both are furnished in the as-fabricated (no temper or treatment) condition. There are 17 material properties with values for both materials. Properties with values for just one material (10, in this case) are not shown.

For each property being compared, the top bar is solder alloy 104 and the bottom bar is 50Cr-50Ni-Cb alloy.

Metric UnitsUS Customary Units

Mechanical Properties

Elastic (Young's, Tensile) Modulus, GPa 37
210
Elongation at Break, % 46
5.6
Poisson's Ratio 0.39
0.26
Shear Modulus, GPa 13
84
Tensile Strength: Ultimate (UTS), MPa 51
620

Thermal Properties

Latent Heat of Fusion, J/g 45
350
Specific Heat Capacity, J/kg-K 180
480
Thermal Expansion, µm/m-K 25
15

Otherwise Unclassified Properties

Density, g/cm3 8.9
8.0
Embodied Carbon, kg CO2/kg material 10
9.2
Embodied Energy, MJ/kg 180
130
Embodied Water, L/kg 900
350

Common Calculations

Stiffness to Weight: Axial, points 2.3
15
Stiffness to Weight: Bending, points 12
25
Strength to Weight: Axial, points 1.6
21
Strength to Weight: Bending, points 3.4
20
Thermal Shock Resistance, points 4.0
14

Alloy Composition

Aluminum (Al), % 0 to 0.0010
0 to 0.25
Antimony (Sb), % 0 to 0.050
0
Arsenic (As), % 0 to 0.030
0
Bismuth (Bi), % 0 to 0.050
0
Cadmium (Cd), % 0 to 0.0020
0
Carbon (C), % 0
0 to 0.1
Chromium (Cr), % 0
47 to 52
Copper (Cu), % 0 to 0.080
0
Gold (Au), % 0 to 0.050
0
Indium (In), % 0 to 0.1
0
Iron (Fe), % 0 to 0.020
0 to 1.0
Lead (Pb), % 39 to 40.5
0
Manganese (Mn), % 0
0 to 0.3
Nickel (Ni), % 0 to 0.010
43.3 to 51.6
Niobium (Nb), % 0
1.4 to 1.7
Nitrogen (N), % 0
0 to 0.16
Phosphorus (P), % 0
0 to 0.020
Silicon (Si), % 0
0 to 0.5
Silver (Ag), % 0 to 0.1
0
Sulfur (S), % 0
0 to 0.020
Tin (Sn), % 59.5 to 60.5
0
Titanium (Ti), % 0
0 to 0.5
Zinc (Zn), % 0 to 0.0010
0