Solder Alloy 104 vs. 70Ag-30Ni Alloy

Both solder alloy 104 and 70Ag-30Ni alloy are otherwise unclassified metals. There are 17 material properties with values for both materials. Properties with values for just one material (6, in this case) are not shown.

For each property being compared, the top bar is solder alloy 104 and the bottom bar is 70Ag-30Ni alloy.

Metric UnitsUS Customary Units

Mechanical Properties

Elastic (Young's, Tensile) Modulus, GPa 37
100
Poisson's Ratio 0.39
0.35
Shear Modulus, GPa 13
39
Tensile Strength: Ultimate (UTS), MPa 51
320 to 530

Thermal Properties

Latent Heat of Fusion, J/g 45
170
Melting Completion (Liquidus), °C 190
960
Melting Onset (Solidus), °C 180
960
Specific Heat Capacity, J/kg-K 180
300
Thermal Expansion, µm/m-K 25
17

Electrical Properties

Electrical Conductivity: Equal Volume, % IACS 11
69
Electrical Conductivity: Equal Weight (Specific), % IACS 11
62

Otherwise Unclassified Properties

Density, g/cm3 8.9
10

Common Calculations

Stiffness to Weight: Axial, points 2.3
5.8
Stiffness to Weight: Bending, points 12
16
Strength to Weight: Axial, points 1.6
8.8 to 15
Strength to Weight: Bending, points 3.4
10 to 15
Thermal Shock Resistance, points 4.0
13 to 21

Alloy Composition


Deprecated: Automatic conversion of false to array is deprecated in /home/public/compare.php on line 460
Aluminum (Al), % 0 to 0.0010
0
Antimony (Sb), % 0 to 0.050
0
Arsenic (As), % 0 to 0.030
0
Bismuth (Bi), % 0 to 0.050
0
Cadmium (Cd), % 0 to 0.0020
0
Copper (Cu), % 0 to 0.080
0
Gold (Au), % 0 to 0.050
0
Indium (In), % 0 to 0.1
0
Iron (Fe), % 0 to 0.020
0
Lead (Pb), % 39 to 40.5
0
Nickel (Ni), % 0 to 0.010
28.8 to 31
Silver (Ag), % 0 to 0.1
69 to 71
Tin (Sn), % 59.5 to 60.5
0
Zinc (Zn), % 0 to 0.0010
0
Residuals, % 0
0 to 0.2