Solder Alloy 104 vs. AWS BAg-19

Both solder alloy 104 and AWS BAg-19 are otherwise unclassified metals. Both are furnished in the as-fabricated (no temper or treatment) condition. There are 15 material properties with values for both materials. Properties with values for just one material (9, in this case) are not shown.

For each property being compared, the top bar is solder alloy 104 and the bottom bar is AWS BAg-19.

Metric UnitsUS Customary Units

Mechanical Properties

Elastic (Young's, Tensile) Modulus, GPa 37
74
Poisson's Ratio 0.39
0.37
Shear Modulus, GPa 13
27
Tensile Strength: Ultimate (UTS), MPa 51
140

Thermal Properties

Latent Heat of Fusion, J/g 45
120
Melting Completion (Liquidus), °C 190
890
Melting Onset (Solidus), °C 180
760
Specific Heat Capacity, J/kg-K 180
250
Thermal Expansion, µm/m-K 25
20

Otherwise Unclassified Properties

Density, g/cm3 8.9
10

Common Calculations

Stiffness to Weight: Axial, points 2.3
4.0
Stiffness to Weight: Bending, points 12
14
Strength to Weight: Axial, points 1.6
3.8
Strength to Weight: Bending, points 3.4
5.8
Thermal Shock Resistance, points 4.0
6.9

Alloy Composition


Deprecated: Automatic conversion of false to array is deprecated in /home/public/compare.php on line 460
Aluminum (Al), % 0 to 0.0010
0
Antimony (Sb), % 0 to 0.050
0
Arsenic (As), % 0 to 0.030
0
Bismuth (Bi), % 0 to 0.050
0
Cadmium (Cd), % 0 to 0.0020
0
Copper (Cu), % 0 to 0.080
6.6 to 7.9
Gold (Au), % 0 to 0.050
0
Indium (In), % 0 to 0.1
0
Iron (Fe), % 0 to 0.020
0
Lead (Pb), % 39 to 40.5
0
Lithium (Li), % 0
0.15 to 0.3
Nickel (Ni), % 0 to 0.010
0
Silver (Ag), % 0 to 0.1
92 to 93
Tin (Sn), % 59.5 to 60.5
0
Zinc (Zn), % 0 to 0.0010
0
Residuals, % 0
0 to 0.15