Solder Alloy 104 vs. Grade 360 Molybdenum

Both solder alloy 104 and grade 360 molybdenum are otherwise unclassified metals. There are 17 material properties with values for both materials. Properties with values for just one material (9, in this case) are not shown.

For each property being compared, the top bar is solder alloy 104 and the bottom bar is grade 360 molybdenum.

Metric UnitsUS Customary Units

Mechanical Properties

Elastic (Young's, Tensile) Modulus, GPa 37
310
Elongation at Break, % 46
6.3 to 17
Poisson's Ratio 0.39
0.31
Shear Modulus, GPa 13
120
Tensile Strength: Ultimate (UTS), MPa 51
430 to 620

Thermal Properties

Latent Heat of Fusion, J/g 45
370
Specific Heat Capacity, J/kg-K 180
250
Thermal Expansion, µm/m-K 25
7.0

Otherwise Unclassified Properties

Density, g/cm3 8.9
10
Embodied Carbon, kg CO2/kg material 10
28
Embodied Energy, MJ/kg 180
330
Embodied Water, L/kg 900
360

Common Calculations

Stiffness to Weight: Axial, points 2.3
17
Stiffness to Weight: Bending, points 12
22
Strength to Weight: Axial, points 1.6
12 to 17
Strength to Weight: Bending, points 3.4
12 to 16
Thermal Shock Resistance, points 4.0
14 to 21

Alloy Composition

Aluminum (Al), % 0 to 0.0010
0
Antimony (Sb), % 0 to 0.050
0
Arsenic (As), % 0 to 0.030
0
Bismuth (Bi), % 0 to 0.050
0
Cadmium (Cd), % 0 to 0.0020
0
Carbon (C), % 0
0 to 0.030
Copper (Cu), % 0 to 0.080
0
Gold (Au), % 0 to 0.050
0
Indium (In), % 0 to 0.1
0
Iron (Fe), % 0 to 0.020
0 to 0.010
Lead (Pb), % 39 to 40.5
0
Molybdenum (Mo), % 0
99.9 to 100
Nickel (Ni), % 0 to 0.010
0 to 0.0020
Nitrogen (N), % 0
0 to 0.0020
Oxygen (O), % 0
0 to 0.0015
Silicon (Si), % 0
0 to 0.010
Silver (Ag), % 0 to 0.1
0
Tin (Sn), % 59.5 to 60.5
0
Zinc (Zn), % 0 to 0.0010
0