Solder Alloy 104 vs. Solder Alloy 124

Both solder alloy 104 and solder alloy 124 are otherwise unclassified metals. Both are furnished in the as-fabricated (no temper or treatment) condition. They have 42% of their average alloy composition in common. There are 23 material properties with values for both materials. Properties with values for just one material (1, in this case) are not shown.

For each property being compared, the top bar is solder alloy 104 and the bottom bar is solder alloy 124.

Metric UnitsUS Customary Units

Mechanical Properties

Elastic (Young's, Tensile) Modulus, GPa 37
17
Elongation at Break, % 46
46
Poisson's Ratio 0.39
0.44
Shear Modulus, GPa 13
5.8
Tensile Strength: Ultimate (UTS), MPa 51
27

Thermal Properties

Latent Heat of Fusion, J/g 45
24
Melting Completion (Liquidus), °C 190
330
Melting Onset (Solidus), °C 180
320
Specific Heat Capacity, J/kg-K 180
130
Thermal Conductivity, W/m-K 50
22
Thermal Expansion, µm/m-K 25
29

Electrical Properties

Electrical Conductivity: Equal Volume, % IACS 11
9.6
Electrical Conductivity: Equal Weight (Specific), % IACS 11
7.7

Otherwise Unclassified Properties

Density, g/cm3 8.9
11
Embodied Carbon, kg CO2/kg material 10
4.1
Embodied Energy, MJ/kg 180
68
Embodied Water, L/kg 900
470

Common Calculations

Stiffness to Weight: Axial, points 2.3
0.83
Stiffness to Weight: Bending, points 12
7.6
Strength to Weight: Axial, points 1.6
0.65
Strength to Weight: Bending, points 3.4
1.8
Thermal Diffusivity, mm2/s 30
15
Thermal Shock Resistance, points 4.0
3.9

Alloy Composition

Aluminum (Al), % 0 to 0.0010
0 to 0.0010
Antimony (Sb), % 0 to 0.050
0 to 0.12
Arsenic (As), % 0 to 0.030
0 to 0.030
Bismuth (Bi), % 0 to 0.050
0 to 0.1
Cadmium (Cd), % 0 to 0.0020
0 to 0.0020
Copper (Cu), % 0 to 0.080
0 to 0.080
Gold (Au), % 0 to 0.050
0 to 0.050
Indium (In), % 0 to 0.1
0 to 0.1
Iron (Fe), % 0 to 0.020
0 to 0.020
Lead (Pb), % 39 to 40.5
97.2 to 98.2
Nickel (Ni), % 0 to 0.010
0 to 0.010
Silver (Ag), % 0 to 0.1
0 to 0.1
Tin (Sn), % 59.5 to 60.5
1.8 to 2.2
Zinc (Zn), % 0 to 0.0010
0 to 0.0010