Solder Alloy 104 vs. Low-oxygen Zirconium

Both solder alloy 104 and low-oxygen zirconium are otherwise unclassified metals. There are 17 material properties with values for both materials. Properties with values for just one material (9, in this case) are not shown.

For each property being compared, the top bar is solder alloy 104 and the bottom bar is low-oxygen zirconium.

Metric UnitsUS Customary Units

Mechanical Properties

Elastic (Young's, Tensile) Modulus, GPa 37
98
Elongation at Break, % 46
23
Poisson's Ratio 0.39
0.34
Shear Modulus, GPa 13
37
Tensile Strength: Ultimate (UTS), MPa 51
330

Thermal Properties

Latent Heat of Fusion, J/g 45
250
Specific Heat Capacity, J/kg-K 180
270
Thermal Conductivity, W/m-K 50
22
Thermal Expansion, µm/m-K 25
5.7

Otherwise Unclassified Properties

Density, g/cm3 8.9
6.7
Embodied Water, L/kg 900
450

Common Calculations

Stiffness to Weight: Axial, points 2.3
8.1
Stiffness to Weight: Bending, points 12
23
Strength to Weight: Axial, points 1.6
14
Strength to Weight: Bending, points 3.4
16
Thermal Diffusivity, mm2/s 30
12
Thermal Shock Resistance, points 4.0
42

Alloy Composition

Aluminum (Al), % 0 to 0.0010
0
Antimony (Sb), % 0 to 0.050
0
Arsenic (As), % 0 to 0.030
0
Bismuth (Bi), % 0 to 0.050
0
Cadmium (Cd), % 0 to 0.0020
0
Carbon (C), % 0
0 to 0.050
Chromium (Cr), % 0
0 to 0.2
Copper (Cu), % 0 to 0.080
0
Gold (Au), % 0 to 0.050
0
Hafnium (Hf), % 0
0 to 4.5
Hydrogen (H), % 0
0 to 0.0050
Indium (In), % 0 to 0.1
0
Iron (Fe), % 0 to 0.020
0 to 0.2
Lead (Pb), % 39 to 40.5
0
Nickel (Ni), % 0 to 0.010
0
Nitrogen (N), % 0
0 to 0.025
Oxygen (O), % 0
0 to 0.1
Silver (Ag), % 0 to 0.1
0
Tin (Sn), % 59.5 to 60.5
0
Zinc (Zn), % 0 to 0.0010
0
Zirconium (Zr), % 0
94.7 to 100