Solder Alloy 104 vs. R58150 Titanium
Solder alloy 104 belongs to the otherwise unclassified metals classification, while R58150 titanium belongs to the titanium alloys. There are 19 material properties with values for both materials. Properties with values for just one material (12, in this case) are not shown.
For each property being compared, the top bar is solder alloy 104 and the bottom bar is R58150 titanium.
Metric UnitsUS Customary Units
Mechanical Properties
| Elastic (Young's, Tensile) Modulus, GPa | 37 | |
| 140 |
| Elongation at Break, % | 46 | |
| 13 |
| Poisson's Ratio | 0.39 | |
| 0.32 |
| Shear Modulus, GPa | 13 | |
| 52 |
| Tensile Strength: Ultimate (UTS), MPa | 51 | |
| 770 |
Thermal Properties
| Latent Heat of Fusion, J/g | 45 | |
| 410 |
| Melting Completion (Liquidus), °C | 190 | |
| 1760 |
| Melting Onset (Solidus), °C | 180 | |
| 1700 |
| Specific Heat Capacity, J/kg-K | 180 | |
| 500 |
| Thermal Expansion, µm/m-K | 25 | |
| 8.4 |
Otherwise Unclassified Properties
| Density, g/cm3 | 8.9 | |
| 5.4 |
| Embodied Carbon, kg CO2/kg material | 10 | |
| 31 |
| Embodied Energy, MJ/kg | 180 | |
| 480 |
| Embodied Water, L/kg | 900 | |
| 150 |
Common Calculations
| Stiffness to Weight: Axial, points | 2.3 | |
| 14 |
| Stiffness to Weight: Bending, points | 12 | |
| 32 |
| Strength to Weight: Axial, points | 1.6 | |
| 40 |
| Strength to Weight: Bending, points | 3.4 | |
| 35 |
| Thermal Shock Resistance, points | 4.0 | |
| 48 |
Alloy Composition
| Aluminum (Al), % | 0 to 0.0010 | |
| 0 |
| Antimony (Sb), % | 0 to 0.050 | |
| 0 |
| Arsenic (As), % | 0 to 0.030 | |
| 0 |
| Bismuth (Bi), % | 0 to 0.050 | |
| 0 |
| Cadmium (Cd), % | 0 to 0.0020 | |
| 0 |
| Carbon (C), % | 0 | |
| 0 to 0.1 |
| Copper (Cu), % | 0 to 0.080 | |
| 0 |
| Gold (Au), % | 0 to 0.050 | |
| 0 |
| Hydrogen (H), % | 0 | |
| 0 to 0.015 |
| Indium (In), % | 0 to 0.1 | |
| 0 |
| Iron (Fe), % | 0 to 0.020 | |
| 0 to 0.1 |
| Lead (Pb), % | 39 to 40.5 | |
| 0 |
| Molybdenum (Mo), % | 0 | |
| 14 to 16 |
| Nickel (Ni), % | 0 to 0.010 | |
| 0 |
| Nitrogen (N), % | 0 | |
| 0 to 0.050 |
| Oxygen (O), % | 0 | |
| 0 to 0.2 |
| Silver (Ag), % | 0 to 0.1 | |
| 0 |
| Tin (Sn), % | 59.5 to 60.5 | |
| 0 |
| Titanium (Ti), % | 0 | |
| 83.5 to 86 |
| Zinc (Zn), % | 0 to 0.0010 | |
| 0 |