Solder Alloy 111 vs. AWS BAg-4

Both solder alloy 111 and AWS BAg-4 are otherwise unclassified metals. Both are furnished in the as-fabricated (no temper or treatment) condition. There are 17 material properties with values for both materials. Properties with values for just one material (8, in this case) are not shown.

For each property being compared, the top bar is solder alloy 111 and the bottom bar is AWS BAg-4.

Metric UnitsUS Customary Units

Mechanical Properties

Elastic (Young's, Tensile) Modulus, GPa 33
91
Poisson's Ratio 0.4
0.33
Shear Modulus, GPa 12
34
Tensile Strength: Ultimate (UTS), MPa 41
150

Thermal Properties

Latent Heat of Fusion, J/g 41
140
Melting Completion (Liquidus), °C 220
780
Melting Onset (Solidus), °C 180
670
Specific Heat Capacity, J/kg-K 180
330
Thermal Expansion, µm/m-K 26
21

Otherwise Unclassified Properties

Density, g/cm3 9.3
8.9
Embodied Carbon, kg CO2/kg material 9.4
40
Embodied Energy, MJ/kg 160
630

Common Calculations

Stiffness to Weight: Axial, points 2.0
5.7
Stiffness to Weight: Bending, points 12
17
Strength to Weight: Axial, points 1.2
4.7
Strength to Weight: Bending, points 2.8
7.1
Thermal Shock Resistance, points 3.5
5.7

Alloy Composition


Deprecated: Automatic conversion of false to array is deprecated in /home/public/compare.php on line 460
Aluminum (Al), % 0 to 0.0010
0
Antimony (Sb), % 0 to 0.2
0
Arsenic (As), % 0 to 0.030
0
Bismuth (Bi), % 0 to 0.1
0
Cadmium (Cd), % 0 to 0.0020
0
Copper (Cu), % 0 to 0.080
29 to 31
Gold (Au), % 0 to 0.050
0
Indium (In), % 0 to 0.1
0
Iron (Fe), % 0 to 0.020
0
Lead (Pb), % 48.8 to 50.5
0
Nickel (Ni), % 0 to 0.010
1.5 to 2.5
Silver (Ag), % 0 to 0.1
39 to 41
Tin (Sn), % 49.5 to 50.5
0
Zinc (Zn), % 0 to 0.0010
26 to 30
Residuals, % 0
0 to 0.15