MakeItFrom.com
Menu (ESC)

Solder Alloy 111 vs. N07716 Nickel

Solder alloy 111 belongs to the otherwise unclassified metals classification, while N07716 nickel belongs to the nickel alloys. There are 23 material properties with values for both materials. Properties with values for just one material (9, in this case) are not shown.

For each property being compared, the top bar is solder alloy 111 and the bottom bar is N07716 nickel.

Metric UnitsUS Customary Units

Mechanical Properties

Elastic (Young's, Tensile) Modulus, GPa 33
200
Elongation at Break, % 35
34
Poisson's Ratio 0.4
0.29
Shear Modulus, GPa 12
78
Tensile Strength: Ultimate (UTS), MPa 41
860

Thermal Properties

Latent Heat of Fusion, J/g 41
320
Melting Completion (Liquidus), °C 220
1480
Melting Onset (Solidus), °C 180
1430
Specific Heat Capacity, J/kg-K 180
440
Thermal Conductivity, W/m-K 48
11
Thermal Expansion, µm/m-K 26
13

Electrical Properties

Electrical Conductivity: Equal Volume, % IACS 11
1.4
Electrical Conductivity: Equal Weight (Specific), % IACS 11
1.5

Otherwise Unclassified Properties

Density, g/cm3 9.3
8.5
Embodied Carbon, kg CO2/kg material 9.4
13
Embodied Energy, MJ/kg 160
190
Embodied Water, L/kg 830
280

Common Calculations

Stiffness to Weight: Axial, points 2.0
13
Stiffness to Weight: Bending, points 12
23
Strength to Weight: Axial, points 1.2
28
Strength to Weight: Bending, points 2.8
24
Thermal Diffusivity, mm2/s 29
2.8
Thermal Shock Resistance, points 3.5
24

Alloy Composition

Aluminum (Al), % 0 to 0.0010
0 to 0.35
Antimony (Sb), % 0 to 0.2
0
Arsenic (As), % 0 to 0.030
0
Bismuth (Bi), % 0 to 0.1
0
Cadmium (Cd), % 0 to 0.0020
0
Carbon (C), % 0
0 to 0.030
Chromium (Cr), % 0
19 to 22
Copper (Cu), % 0 to 0.080
0
Gold (Au), % 0 to 0.050
0
Indium (In), % 0 to 0.1
0
Iron (Fe), % 0 to 0.020
0 to 11.3
Lead (Pb), % 48.8 to 50.5
0
Manganese (Mn), % 0
0 to 0.2
Molybdenum (Mo), % 0
7.0 to 9.5
Nickel (Ni), % 0 to 0.010
59 to 63
Niobium (Nb), % 0
2.8 to 4.0
Phosphorus (P), % 0
0 to 0.015
Silicon (Si), % 0
0 to 0.2
Silver (Ag), % 0 to 0.1
0
Sulfur (S), % 0
0 to 0.010
Tin (Sn), % 49.5 to 50.5
0
Titanium (Ti), % 0
1.0 to 1.6
Zinc (Zn), % 0 to 0.0010
0