Solder Alloy 111 vs. Zamak 2

Solder alloy 111 belongs to the otherwise unclassified metals classification, while Zamak 2 belongs to the zinc alloys. There are 24 material properties with values for both materials. Properties with values for just one material (11, in this case) are not shown.

For each property being compared, the top bar is solder alloy 111 and the bottom bar is Zamak 2.

Metric UnitsUS Customary Units

Mechanical Properties

Brinell Hardness 14
100
Elastic (Young's, Tensile) Modulus, GPa 33
87
Elongation at Break, % 35
6.0
Poisson's Ratio 0.4
0.26
Shear Modulus, GPa 12
33
Tensile Strength: Ultimate (UTS), MPa 41
360

Thermal Properties

Latent Heat of Fusion, J/g 41
130
Melting Completion (Liquidus), °C 220
390
Melting Onset (Solidus), °C 180
380
Specific Heat Capacity, J/kg-K 180
410
Thermal Conductivity, W/m-K 48
110
Thermal Expansion, µm/m-K 26
28

Electrical Properties

Electrical Conductivity: Equal Volume, % IACS 11
25
Electrical Conductivity: Equal Weight (Specific), % IACS 11
35

Otherwise Unclassified Properties

Density, g/cm3 9.3
6.5
Embodied Carbon, kg CO2/kg material 9.4
3.0
Embodied Energy, MJ/kg 160
57
Embodied Water, L/kg 830
380

Common Calculations

Stiffness to Weight: Axial, points 2.0
7.5
Stiffness to Weight: Bending, points 12
23
Strength to Weight: Axial, points 1.2
15
Strength to Weight: Bending, points 2.8
17
Thermal Diffusivity, mm2/s 29
41
Thermal Shock Resistance, points 3.5
11

Alloy Composition

Aluminum (Al), % 0 to 0.0010
3.5 to 4.3
Antimony (Sb), % 0 to 0.2
0
Arsenic (As), % 0 to 0.030
0
Bismuth (Bi), % 0 to 0.1
0
Cadmium (Cd), % 0 to 0.0020
0 to 0.0050
Copper (Cu), % 0 to 0.080
2.5 to 3.3
Gold (Au), % 0 to 0.050
0
Indium (In), % 0 to 0.1
0
Iron (Fe), % 0 to 0.020
0 to 0.1
Lead (Pb), % 48.8 to 50.5
0 to 0.0050
Magnesium (Mg), % 0
0.020 to 0.060
Nickel (Ni), % 0 to 0.010
0 to 0.020
Silicon (Si), % 0
0 to 0.030
Silver (Ag), % 0 to 0.1
0
Tin (Sn), % 49.5 to 50.5
0 to 0.0030
Zinc (Zn), % 0 to 0.0010
92.2 to 94