Solder Alloy 115 vs. ISO-WD43150 Magnesium
Solder alloy 115 belongs to the otherwise unclassified metals classification, while ISO-WD43150 magnesium belongs to the magnesium alloys. There are 24 material properties with values for both materials. Properties with values for just one material (7, in this case) are not shown. Please note that the two materials have significantly dissimilar densities. This means that additional care is required when interpreting the data, because some material properties are based on units of mass, while others are based on units of area or volume.
For each property being compared, the top bar is solder alloy 115 and the bottom bar is ISO-WD43150 magnesium.
Metric UnitsUS Customary Units
Mechanical Properties
| Elastic (Young's, Tensile) Modulus, GPa | 28 | |
| 45 |
| Elongation at Break, % | 22 | |
| 2.8 |
| Poisson's Ratio | 0.41 | |
| 0.29 |
| Shear Modulus, GPa | 10 | |
| 18 |
| Tensile Strength: Ultimate (UTS), MPa | 36 | |
| 250 |
Thermal Properties
| Latent Heat of Fusion, J/g | 36 | |
| 350 |
| Melting Completion (Liquidus), °C | 250 | |
| 610 |
| Melting Onset (Solidus), °C | 180 | |
| 590 |
| Specific Heat Capacity, J/kg-K | 160 | |
| 990 |
| Thermal Conductivity, W/m-K | 43 | |
| 140 |
| Thermal Expansion, µm/m-K | 27 | |
| 27 |
Electrical Properties
| Electrical Conductivity: Equal Volume, % IACS | 9.8 | |
| 31 |
| Electrical Conductivity: Equal Weight (Specific), % IACS | 8.9 | |
| 170 |
Otherwise Unclassified Properties
| Base Metal Price, % relative | 95 | |
| 12 |
| Density, g/cm3 | 9.9 | |
| 1.7 |
| Embodied Carbon, kg CO2/kg material | 7.8 | |
| 24 |
| Embodied Energy, MJ/kg | 130 | |
| 160 |
| Embodied Water, L/kg | 730 | |
| 970 |
Common Calculations
| Stiffness to Weight: Axial, points | 1.6 | |
| 15 |
| Stiffness to Weight: Bending, points | 10 | |
| 71 |
| Strength to Weight: Axial, points | 1.0 | |
| 41 |
| Strength to Weight: Bending, points | 2.4 | |
| 52 |
| Thermal Diffusivity, mm2/s | 27 | |
| 81 |
| Thermal Shock Resistance, points | 3.4 | |
| 14 |
Alloy Composition
Deprecated: Automatic conversion of false to array is deprecated in /home/public/compare.php on line 460
| Aluminum (Al), % | 0 to 0.0010 | |
| 0 |
| Antimony (Sb), % | 0 to 0.5 | |
| 0 |
| Arsenic (As), % | 0 to 0.030 | |
| 0 |
| Bismuth (Bi), % | 0 to 0.25 | |
| 0 |
| Cadmium (Cd), % | 0 to 0.0050 | |
| 0 |
| Copper (Cu), % | 0 to 0.080 | |
| 0 to 0.050 |
| Gold (Au), % | 0 to 0.050 | |
| 0 |
| Indium (In), % | 0 to 0.1 | |
| 0 |
| Iron (Fe), % | 0 to 0.020 | |
| 0 |
| Lead (Pb), % | 63.4 to 65.5 | |
| 0 |
| Magnesium (Mg), % | 0 | |
| 97.5 to 98.8 |
| Manganese (Mn), % | 0 | |
| 1.2 to 2.0 |
| Nickel (Ni), % | 0 to 0.010 | |
| 0 to 0.010 |
| Silicon (Si), % | 0 | |
| 0 to 0.1 |
| Silver (Ag), % | 0 to 0.1 | |
| 0 |
| Tin (Sn), % | 34.5 to 35.5 | |
| 0 |
| Zinc (Zn), % | 0 to 0.0010 | |
| 0 |
| Residuals, % | 0 | |
| 0 to 0.3 |