Solder Alloy 122 vs. Class 1 Tungsten
Both solder alloy 122 and class 1 tungsten are otherwise unclassified metals. Both are furnished in the as-fabricated (no temper or treatment) condition. There are 21 material properties with values for both materials. Properties with values for just one material (8, in this case) are not shown.
For each property being compared, the top bar is solder alloy 122 and the bottom bar is class 1 tungsten.
Metric UnitsUS Customary Units
Mechanical Properties
| Elastic (Young's, Tensile) Modulus, GPa | 20 | |
| 250 |
| Elongation at Break, % | 30 | |
| 5.7 |
| Poisson's Ratio | 0.43 | |
| 0.29 |
| Shear Modulus, GPa | 6.9 | |
| 98 |
| Tensile Strength: Ultimate (UTS), MPa | 30 | |
| 860 |
Thermal Properties
| Latent Heat of Fusion, J/g | 27 | |
| 160 |
| Specific Heat Capacity, J/kg-K | 140 | |
| 120 |
| Thermal Conductivity, W/m-K | 25 | |
| 21 |
| Thermal Expansion, µm/m-K | 28 | |
| 5.1 |
Electrical Properties
| Electrical Conductivity: Equal Volume, % IACS | 8.9 | |
| 12 |
| Electrical Conductivity: Equal Weight (Specific), % IACS | 7.3 | |
| 7.4 |
Otherwise Unclassified Properties
| Density, g/cm3 | 11 | |
| 15 |
| Embodied Carbon, kg CO2/kg material | 5.0 | |
| 22 |
| Embodied Energy, MJ/kg | 84 | |
| 340 |
| Embodied Water, L/kg | 540 | |
| 140 |
Common Calculations
| Stiffness to Weight: Axial, points | 1.0 | |
| 9.6 |
| Stiffness to Weight: Bending, points | 8.2 | |
| 14 |
| Strength to Weight: Axial, points | 0.77 | |
| 16 |
| Strength to Weight: Bending, points | 2.0 | |
| 14 |
| Thermal Diffusivity, mm2/s | 17 | |
| 12 |
| Thermal Shock Resistance, points | 3.9 | |
| 48 |
Alloy Composition
Deprecated: Automatic conversion of false to array is deprecated in /home/public/compare.php on line 460
| Aluminum (Al), % | 0 to 0.0010 | |
| 0 |
| Antimony (Sb), % | 0 to 0.5 | |
| 0 |
| Arsenic (As), % | 0 to 0.030 | |
| 0 |
| Bismuth (Bi), % | 0 to 0.25 | |
| 0 |
| Cadmium (Cd), % | 0 to 0.0050 | |
| 0 |
| Copper (Cu), % | 0 to 0.080 | |
| 0 |
| Gold (Au), % | 0 to 0.050 | |
| 0 |
| Indium (In), % | 0 to 0.1 | |
| 0 |
| Iron (Fe), % | 0 to 0.020 | |
| 0 |
| Lead (Pb), % | 88.4 to 90.5 | |
| 0 |
| Nickel (Ni), % | 0 to 0.010 | |
| 0 |
| Silver (Ag), % | 0 to 0.1 | |
| 0 |
| Tin (Sn), % | 9.5 to 10.5 | |
| 0 |
| Tungsten (W), % | 0 | |
| 90 |
| Zinc (Zn), % | 0 to 0.0010 | |
| 0 |
| Residuals, % | 0 | |
| 10 |