Solder Alloy 122 vs. Grade 704C Zirconium
Both solder alloy 122 and grade 704C zirconium are otherwise unclassified metals. Both are furnished in the as-fabricated (no temper or treatment) condition. There are 18 material properties with values for both materials. Properties with values for just one material (11, in this case) are not shown.
For each property being compared, the top bar is solder alloy 122 and the bottom bar is grade 704C zirconium.
Metric UnitsUS Customary Units
Mechanical Properties
| Brinell Hardness | 10 | |
| 210 |
| Elastic (Young's, Tensile) Modulus, GPa | 20 | |
| 97 |
| Elongation at Break, % | 30 | |
| 11 |
| Poisson's Ratio | 0.43 | |
| 0.34 |
| Shear Modulus, GPa | 6.9 | |
| 36 |
| Tensile Strength: Ultimate (UTS), MPa | 30 | |
| 470 |
Thermal Properties
| Latent Heat of Fusion, J/g | 27 | |
| 240 |
| Specific Heat Capacity, J/kg-K | 140 | |
| 270 |
| Thermal Conductivity, W/m-K | 25 | |
| 21 |
| Thermal Expansion, µm/m-K | 28 | |
| 5.9 |
Otherwise Unclassified Properties
| Density, g/cm3 | 11 | |
| 6.7 |
| Embodied Water, L/kg | 540 | |
| 460 |
Common Calculations
| Stiffness to Weight: Axial, points | 1.0 | |
| 8.1 |
| Stiffness to Weight: Bending, points | 8.2 | |
| 23 |
| Strength to Weight: Axial, points | 0.77 | |
| 20 |
| Strength to Weight: Bending, points | 2.0 | |
| 20 |
| Thermal Diffusivity, mm2/s | 17 | |
| 12 |
| Thermal Shock Resistance, points | 3.9 | |
| 58 |
Alloy Composition
| Aluminum (Al), % | 0 to 0.0010 | |
| 0 |
| Antimony (Sb), % | 0 to 0.5 | |
| 0 |
| Arsenic (As), % | 0 to 0.030 | |
| 0 |
| Bismuth (Bi), % | 0 to 0.25 | |
| 0 |
| Cadmium (Cd), % | 0 to 0.0050 | |
| 0 |
| Carbon (C), % | 0 | |
| 0 to 0.1 |
| Copper (Cu), % | 0 to 0.080 | |
| 0 |
| Gold (Au), % | 0 to 0.050 | |
| 0 |
| Hafnium (Hf), % | 0 | |
| 0 to 4.5 |
| Hydrogen (H), % | 0 | |
| 0 to 0.0050 |
| Indium (In), % | 0 to 0.1 | |
| 0 |
| Iron (Fe), % | 0 to 0.020 | |
| 0 to 0.3 |
| Lead (Pb), % | 88.4 to 90.5 | |
| 0 |
| Nickel (Ni), % | 0 to 0.010 | |
| 0 |
| Nitrogen (N), % | 0 | |
| 0 to 0.030 |
| Oxygen (O), % | 0 | |
| 0 to 0.3 |
| Phosphorus (P), % | 0 | |
| 0 to 0.010 |
| Silver (Ag), % | 0 to 0.1 | |
| 0 |
| Tin (Sn), % | 9.5 to 10.5 | |
| 1.0 to 2.0 |
| Zinc (Zn), % | 0 to 0.0010 | |
| 0 |
| Zirconium (Zr), % | 0 | |
| 92.9 to 99 |