Solder Alloy 123 vs. Z20301 Zinc
Solder alloy 123 belongs to the otherwise unclassified metals classification, while Z20301 zinc belongs to the zinc alloys. There are 24 material properties with values for both materials. Properties with values for just one material (5, in this case) are not shown.
For each property being compared, the top bar is solder alloy 123 and the bottom bar is Z20301 zinc.
Metric UnitsUS Customary Units
Mechanical Properties
| Elastic (Young's, Tensile) Modulus, GPa | 18 | |
| 87 |
| Elongation at Break, % | 45 | |
| 53 |
| Poisson's Ratio | 0.44 | |
| 0.25 |
| Shear Modulus, GPa | 6.2 | |
| 35 |
| Tensile Strength: Ultimate (UTS), MPa | 28 | |
| 160 |
Thermal Properties
| Latent Heat of Fusion, J/g | 26 | |
| 110 |
| Melting Completion (Liquidus), °C | 310 | |
| 410 |
| Melting Onset (Solidus), °C | 300 | |
| 400 |
| Specific Heat Capacity, J/kg-K | 130 | |
| 390 |
| Thermal Conductivity, W/m-K | 23 | |
| 110 |
| Thermal Expansion, µm/m-K | 29 | |
| 26 |
Electrical Properties
| Electrical Conductivity: Equal Volume, % IACS | 8.8 | |
| 27 |
| Electrical Conductivity: Equal Weight (Specific), % IACS | 7.1 | |
| 37 |
Otherwise Unclassified Properties
| Base Metal Price, % relative | 75 | |
| 11 |
| Density, g/cm3 | 11 | |
| 6.6 |
| Embodied Carbon, kg CO2/kg material | 4.5 | |
| 2.8 |
| Embodied Energy, MJ/kg | 74 | |
| 53 |
| Embodied Water, L/kg | 500 | |
| 340 |
Common Calculations
| Stiffness to Weight: Axial, points | 0.9 | |
| 7.4 |
| Stiffness to Weight: Bending, points | 7.8 | |
| 23 |
| Strength to Weight: Axial, points | 0.69 | |
| 6.7 |
| Strength to Weight: Bending, points | 1.8 | |
| 9.9 |
| Thermal Diffusivity, mm2/s | 16 | |
| 44 |
| Thermal Shock Resistance, points | 3.8 | |
| 5.0 |
Alloy Composition
| Aluminum (Al), % | 0 to 0.0010 | |
| 0 to 0.0020 |
| Antimony (Sb), % | 0 to 0.5 | |
| 0 |
| Arsenic (As), % | 0 to 0.030 | |
| 0 |
| Bismuth (Bi), % | 0 to 0.1 | |
| 0 |
| Cadmium (Cd), % | 0 to 0.0050 | |
| 0 to 0.010 |
| Copper (Cu), % | 0 to 0.080 | |
| 0 to 0.0050 |
| Gold (Au), % | 0 to 0.050 | |
| 0 |
| Indium (In), % | 0 to 0.1 | |
| 0 |
| Iron (Fe), % | 0 to 0.020 | |
| 0 to 0.010 |
| Lead (Pb), % | 93.5 to 95.5 | |
| 0 to 0.1 |
| Nickel (Ni), % | 0 to 0.010 | |
| 0 |
| Silver (Ag), % | 0 to 0.1 | |
| 0 |
| Tin (Sn), % | 4.5 to 5.5 | |
| 0 |
| Titanium (Ti), % | 0 | |
| 0 to 0.020 |
| Zinc (Zn), % | 0 to 0.0010 | |
| 99.853 to 100 |