Solder Alloy 131 vs. 2117 Aluminum

Solder alloy 131 belongs to the otherwise unclassified metals classification, while 2117 aluminum belongs to the aluminum alloys. There are 23 material properties with values for both materials. Properties with values for just one material (8, in this case) are not shown. Please note that the two materials have significantly dissimilar densities. This means that additional care is required when interpreting the data, because some material properties are based on units of mass, while others are based on units of area or volume.

For each property being compared, the top bar is solder alloy 131 and the bottom bar is 2117 aluminum.

Metric UnitsUS Customary Units

Mechanical Properties

Elastic (Young's, Tensile) Modulus, GPa 38
71
Elongation at Break, % 47
26
Poisson's Ratio 0.39
0.33
Shear Modulus, GPa 14
27
Tensile Strength: Ultimate (UTS), MPa 31
300

Thermal Properties

Latent Heat of Fusion, J/g 46
400
Melting Completion (Liquidus), °C 180
650
Melting Onset (Solidus), °C 180
550
Specific Heat Capacity, J/kg-K 190
880
Thermal Conductivity, W/m-K 55
150
Thermal Expansion, µm/m-K 25
24

Electrical Properties

Electrical Conductivity: Equal Volume, % IACS 11
40
Electrical Conductivity: Equal Weight (Specific), % IACS 12
120

Otherwise Unclassified Properties

Density, g/cm3 8.8
3.0
Embodied Carbon, kg CO2/kg material 11
8.2
Embodied Energy, MJ/kg 180
150
Embodied Water, L/kg 940
1150

Common Calculations

Stiffness to Weight: Axial, points 2.4
13
Stiffness to Weight: Bending, points 13
47
Strength to Weight: Axial, points 1.0
28
Strength to Weight: Bending, points 2.5
33
Thermal Diffusivity, mm2/s 33
59
Thermal Shock Resistance, points 2.4
12

Alloy Composition


Deprecated: Automatic conversion of false to array is deprecated in /home/public/compare.php on line 460
Aluminum (Al), % 0 to 0.0010
91 to 97.6
Antimony (Sb), % 0.2 to 0.5
0
Arsenic (As), % 0 to 0.030
0
Bismuth (Bi), % 0 to 0.1
0
Cadmium (Cd), % 0 to 0.0020
0
Chromium (Cr), % 0
0 to 0.1
Copper (Cu), % 0 to 0.080
2.2 to 4.5
Gold (Au), % 0 to 0.050
0
Indium (In), % 0 to 0.1
0
Iron (Fe), % 0 to 0.020
0 to 0.7
Lead (Pb), % 35.5 to 37.3
0
Magnesium (Mg), % 0
0.2 to 1.0
Manganese (Mn), % 0
0.4 to 1.0
Nickel (Ni), % 0 to 0.010
0
Silicon (Si), % 0
0.2 to 0.8
Silver (Ag), % 0 to 0.1
0
Tin (Sn), % 62.5 to 63.5
0
Titanium (Ti), % 0
0 to 0.25
Zinc (Zn), % 0 to 0.0010
0 to 0.25
Zirconium (Zr), % 0
0 to 0.25
Residuals, % 0
0 to 0.15