Solder Alloy 131 vs. AWS BVAg-6b

Both solder alloy 131 and AWS BVAg-6b are otherwise unclassified metals. Both are furnished in the as-fabricated (no temper or treatment) condition. There are 17 material properties with values for both materials. Properties with values for just one material (7, in this case) are not shown.

For each property being compared, the top bar is solder alloy 131 and the bottom bar is AWS BVAg-6b.

Metric UnitsUS Customary Units

Mechanical Properties

Elastic (Young's, Tensile) Modulus, GPa 38
93
Poisson's Ratio 0.39
0.35
Shear Modulus, GPa 14
35
Tensile Strength: Ultimate (UTS), MPa 31
180

Thermal Properties

Latent Heat of Fusion, J/g 46
160
Melting Completion (Liquidus), °C 180
870
Melting Onset (Solidus), °C 180
780
Specific Heat Capacity, J/kg-K 190
310
Thermal Expansion, µm/m-K 25
19

Otherwise Unclassified Properties

Density, g/cm3 8.8
9.7
Embodied Carbon, kg CO2/kg material 11
49
Embodied Energy, MJ/kg 180
770

Common Calculations

Stiffness to Weight: Axial, points 2.4
5.3
Stiffness to Weight: Bending, points 13
16
Strength to Weight: Axial, points 1.0
5.1
Strength to Weight: Bending, points 2.5
7.3
Thermal Shock Resistance, points 2.4
7.4

Alloy Composition

Aluminum (Al), % 0 to 0.0010
0
Antimony (Sb), % 0.2 to 0.5
0
Arsenic (As), % 0 to 0.030
0
Bismuth (Bi), % 0 to 0.1
0
Cadmium (Cd), % 0 to 0.0020
0 to 0.0010
Carbon (C), % 0
0 to 0.0050
Copper (Cu), % 0 to 0.080
49 to 51
Gold (Au), % 0 to 0.050
0
Indium (In), % 0 to 0.1
0
Iron (Fe), % 0 to 0.020
0
Lead (Pb), % 35.5 to 37.3
0 to 0.0020
Nickel (Ni), % 0 to 0.010
0
Phosphorus (P), % 0
0 to 0.0020
Silver (Ag), % 0 to 0.1
49 to 51
Tin (Sn), % 62.5 to 63.5
0
Zinc (Zn), % 0 to 0.0010
0 to 0.0010