Solder Alloy 131 vs. EN 1.4710 Stainless Steel

Solder alloy 131 belongs to the otherwise unclassified metals classification, while EN 1.4710 stainless steel belongs to the iron alloys. There are 19 material properties with values for both materials. Properties with values for just one material (9, in this case) are not shown.

For each property being compared, the top bar is solder alloy 131 and the bottom bar is EN 1.4710 stainless steel.

Metric UnitsUS Customary Units

Mechanical Properties

Elastic (Young's, Tensile) Modulus, GPa 38
190
Elongation at Break, % 47
20
Poisson's Ratio 0.39
0.29
Shear Modulus, GPa 14
74

Thermal Properties

Latent Heat of Fusion, J/g 46
290
Melting Completion (Liquidus), °C 180
1430
Melting Onset (Solidus), °C 180
1390
Specific Heat Capacity, J/kg-K 190
480
Thermal Conductivity, W/m-K 55
24
Thermal Expansion, µm/m-K 25
9.9

Electrical Properties

Electrical Conductivity: Equal Volume, % IACS 11
6.4
Electrical Conductivity: Equal Weight (Specific), % IACS 12
7.5

Otherwise Unclassified Properties

Density, g/cm3 8.8
7.7
Embodied Carbon, kg CO2/kg material 11
1.8
Embodied Energy, MJ/kg 180
24
Embodied Water, L/kg 940
76

Common Calculations

Stiffness to Weight: Axial, points 2.4
14
Stiffness to Weight: Bending, points 13
25
Thermal Diffusivity, mm2/s 33
6.5

Alloy Composition

Aluminum (Al), % 0 to 0.0010
0
Antimony (Sb), % 0.2 to 0.5
0
Arsenic (As), % 0 to 0.030
0
Bismuth (Bi), % 0 to 0.1
0
Cadmium (Cd), % 0 to 0.0020
0
Carbon (C), % 0
0.2 to 0.35
Chromium (Cr), % 0
6.0 to 8.0
Copper (Cu), % 0 to 0.080
0
Gold (Au), % 0 to 0.050
0
Indium (In), % 0 to 0.1
0
Iron (Fe), % 0 to 0.020
87.4 to 92.3
Lead (Pb), % 35.5 to 37.3
0
Manganese (Mn), % 0
0.5 to 1.0
Molybdenum (Mo), % 0
0 to 0.15
Nickel (Ni), % 0 to 0.010
0 to 0.5
Phosphorus (P), % 0
0 to 0.035
Silicon (Si), % 0
1.0 to 2.5
Silver (Ag), % 0 to 0.1
0
Sulfur (S), % 0
0 to 0.030
Tin (Sn), % 62.5 to 63.5
0
Zinc (Zn), % 0 to 0.0010
0