Solder Alloy 131 vs. EN AC-47100 Aluminum

Solder alloy 131 belongs to the otherwise unclassified metals classification, while EN AC-47100 aluminum belongs to the aluminum alloys. There are 23 material properties with values for both materials. Properties with values for just one material (7, in this case) are not shown. Please note that the two materials have significantly dissimilar densities. This means that additional care is required when interpreting the data, because some material properties are based on units of mass, while others are based on units of area or volume.

For each property being compared, the top bar is solder alloy 131 and the bottom bar is EN AC-47100 aluminum.

Metric UnitsUS Customary Units

Mechanical Properties

Elastic (Young's, Tensile) Modulus, GPa 38
73
Elongation at Break, % 47
1.1
Poisson's Ratio 0.39
0.33
Shear Modulus, GPa 14
27
Tensile Strength: Ultimate (UTS), MPa 31
270

Thermal Properties

Latent Heat of Fusion, J/g 46
570
Melting Completion (Liquidus), °C 180
590
Melting Onset (Solidus), °C 180
560
Specific Heat Capacity, J/kg-K 190
890
Thermal Conductivity, W/m-K 55
130
Thermal Expansion, µm/m-K 25
21

Electrical Properties

Electrical Conductivity: Equal Volume, % IACS 11
30
Electrical Conductivity: Equal Weight (Specific), % IACS 12
100

Otherwise Unclassified Properties

Density, g/cm3 8.8
2.6
Embodied Carbon, kg CO2/kg material 11
7.6
Embodied Energy, MJ/kg 180
140
Embodied Water, L/kg 940
1030

Common Calculations

Stiffness to Weight: Axial, points 2.4
15
Stiffness to Weight: Bending, points 13
53
Strength to Weight: Axial, points 1.0
28
Strength to Weight: Bending, points 2.5
35
Thermal Diffusivity, mm2/s 33
54
Thermal Shock Resistance, points 2.4
12

Alloy Composition


Deprecated: Automatic conversion of false to array is deprecated in /home/public/compare.php on line 460
Aluminum (Al), % 0 to 0.0010
81.4 to 88.8
Antimony (Sb), % 0.2 to 0.5
0
Arsenic (As), % 0 to 0.030
0
Bismuth (Bi), % 0 to 0.1
0
Cadmium (Cd), % 0 to 0.0020
0
Chromium (Cr), % 0
0 to 0.1
Copper (Cu), % 0 to 0.080
0.7 to 1.2
Gold (Au), % 0 to 0.050
0
Indium (In), % 0 to 0.1
0
Iron (Fe), % 0 to 0.020
0 to 1.3
Lead (Pb), % 35.5 to 37.3
0 to 0.2
Magnesium (Mg), % 0
0 to 0.35
Manganese (Mn), % 0
0 to 0.55
Nickel (Ni), % 0 to 0.010
0 to 0.3
Silicon (Si), % 0
10.5 to 13.5
Silver (Ag), % 0 to 0.1
0
Tin (Sn), % 62.5 to 63.5
0 to 0.1
Titanium (Ti), % 0
0 to 0.2
Zinc (Zn), % 0 to 0.0010
0 to 0.55
Residuals, % 0
0 to 0.25