Solder Alloy 131 vs. Grade 200 Maraging Steel

Solder alloy 131 belongs to the otherwise unclassified metals classification, while grade 200 maraging steel belongs to the iron alloys. There are 19 material properties with values for both materials. Properties with values for just one material (12, in this case) are not shown.

For each property being compared, the top bar is solder alloy 131 and the bottom bar is grade 200 maraging steel.

Metric UnitsUS Customary Units

Mechanical Properties

Elastic (Young's, Tensile) Modulus, GPa 38
190
Elongation at Break, % 47
9.1 to 18
Poisson's Ratio 0.39
0.3
Shear Modulus, GPa 14
74
Tensile Strength: Ultimate (UTS), MPa 31
970 to 1500

Thermal Properties

Latent Heat of Fusion, J/g 46
260
Melting Completion (Liquidus), °C 180
1460
Melting Onset (Solidus), °C 180
1420
Specific Heat Capacity, J/kg-K 190
460
Thermal Expansion, µm/m-K 25
12

Otherwise Unclassified Properties

Density, g/cm3 8.8
8.2
Embodied Carbon, kg CO2/kg material 11
4.5
Embodied Energy, MJ/kg 180
59
Embodied Water, L/kg 940
140

Common Calculations

Stiffness to Weight: Axial, points 2.4
13
Stiffness to Weight: Bending, points 13
23
Strength to Weight: Axial, points 1.0
33 to 51
Strength to Weight: Bending, points 2.5
27 to 35
Thermal Shock Resistance, points 2.4
29 to 45

Alloy Composition

Aluminum (Al), % 0 to 0.0010
0.050 to 0.15
Antimony (Sb), % 0.2 to 0.5
0
Arsenic (As), % 0 to 0.030
0
Bismuth (Bi), % 0 to 0.1
0
Boron (B), % 0
0 to 0.0030
Cadmium (Cd), % 0 to 0.0020
0
Calcium (Ca), % 0
0 to 0.050
Carbon (C), % 0
0 to 0.030
Cobalt (Co), % 0
8.0 to 9.0
Copper (Cu), % 0 to 0.080
0
Gold (Au), % 0 to 0.050
0
Indium (In), % 0 to 0.1
0
Iron (Fe), % 0 to 0.020
67.8 to 71.8
Lead (Pb), % 35.5 to 37.3
0
Manganese (Mn), % 0
0 to 0.1
Molybdenum (Mo), % 0
3.0 to 3.5
Nickel (Ni), % 0 to 0.010
17 to 19
Phosphorus (P), % 0
0 to 0.010
Silicon (Si), % 0
0 to 0.1
Silver (Ag), % 0 to 0.1
0
Sulfur (S), % 0
0 to 0.010
Tin (Sn), % 62.5 to 63.5
0
Titanium (Ti), % 0
0.15 to 0.25
Zinc (Zn), % 0 to 0.0010
0
Zirconium (Zr), % 0
0 to 0.020