Solder Alloy 132 vs. Grade 705C Zirconium

Both solder alloy 132 and grade 705C zirconium are otherwise unclassified metals. Both are furnished in the as-fabricated (no temper or treatment) condition. There are 17 material properties with values for both materials. Properties with values for just one material (11, in this case) are not shown.

For each property being compared, the top bar is solder alloy 132 and the bottom bar is grade 705C zirconium.

Metric UnitsUS Customary Units

Mechanical Properties

Elastic (Young's, Tensile) Modulus, GPa 37
98
Elongation at Break, % 43
13
Poisson's Ratio 0.39
0.34
Shear Modulus, GPa 13
36
Tensile Strength: Ultimate (UTS), MPa 52
540

Thermal Properties

Latent Heat of Fusion, J/g 45
250
Specific Heat Capacity, J/kg-K 180
270
Thermal Conductivity, W/m-K 50
18
Thermal Expansion, µm/m-K 25
5.7

Otherwise Unclassified Properties

Density, g/cm3 8.9
6.7
Embodied Water, L/kg 910
450

Common Calculations

Stiffness to Weight: Axial, points 2.3
8.1
Stiffness to Weight: Bending, points 12
23
Strength to Weight: Axial, points 1.6
22
Strength to Weight: Bending, points 3.5
22
Thermal Diffusivity, mm2/s 30
9.9
Thermal Shock Resistance, points 4.1
69

Alloy Composition

Aluminum (Al), % 0 to 0.0010
0
Antimony (Sb), % 0.2 to 0.5
0
Arsenic (As), % 0 to 0.030
0
Bismuth (Bi), % 0 to 0.1
0
Cadmium (Cd), % 0 to 0.0020
0
Carbon (C), % 0
0 to 0.1
Copper (Cu), % 0 to 0.080
0
Gold (Au), % 0 to 0.050
0
Hafnium (Hf), % 0
0 to 4.5
Hydrogen (H), % 0
0 to 0.0050
Indium (In), % 0 to 0.1
0
Iron (Fe), % 0 to 0.020
0 to 0.3
Lead (Pb), % 38.5 to 40.3
0
Nickel (Ni), % 0 to 0.010
0
Niobium (Nb), % 0
2.0 to 3.0
Nitrogen (N), % 0
0 to 0.030
Oxygen (O), % 0
0 to 0.3
Phosphorus (P), % 0
0 to 0.010
Silver (Ag), % 0 to 0.1
0
Tin (Sn), % 59.5 to 60.5
0
Zinc (Zn), % 0 to 0.0010
0
Zirconium (Zr), % 0
91.9 to 98