Solder Alloy 132 vs. Solder Alloy 141

Both solder alloy 132 and solder alloy 141 are otherwise unclassified metals. Both are furnished in the as-fabricated (no temper or treatment) condition. They have a very high 98% of their average alloy composition in common.

For each property being compared, the top bar is solder alloy 132 and the bottom bar is solder alloy 141.

Metric UnitsUS Customary Units

Mechanical Properties

Elastic (Young's, Tensile) Modulus, GPa 37
37
Elongation at Break, % 43
39
Poisson's Ratio 0.39
0.39
Shear Modulus, GPa 13
13
Tensile Strength: Ultimate (UTS), MPa 52
54

Thermal Properties

Latent Heat of Fusion, J/g 45
46
Melting Completion (Liquidus), °C 190
190
Melting Onset (Solidus), °C 180
180
Specific Heat Capacity, J/kg-K 180
180
Thermal Conductivity, W/m-K 50
48
Thermal Expansion, µm/m-K 25
24

Electrical Properties

Electrical Conductivity: Equal Volume, % IACS 11
10
Electrical Conductivity: Equal Weight (Specific), % IACS 12
10

Otherwise Unclassified Properties

Density, g/cm3 8.9
8.9
Embodied Carbon, kg CO2/kg material 11
11
Embodied Energy, MJ/kg 180
180
Embodied Water, L/kg 910
970

Common Calculations

Stiffness to Weight: Axial, points 2.3
2.3
Stiffness to Weight: Bending, points 12
13
Strength to Weight: Axial, points 1.6
1.7
Strength to Weight: Bending, points 3.5
3.6
Thermal Diffusivity, mm2/s 30
29
Thermal Shock Resistance, points 4.1
4.3

Alloy Composition

Aluminum (Al), % 0 to 0.0010
0 to 0.0010
Antimony (Sb), % 0.2 to 0.5
0 to 0.2
Arsenic (As), % 0 to 0.030
0 to 0.030
Bismuth (Bi), % 0 to 0.1
2.0 to 3.0
Cadmium (Cd), % 0 to 0.0020
0 to 0.0020
Copper (Cu), % 0 to 0.080
0 to 0.080
Gold (Au), % 0 to 0.050
0 to 0.050
Indium (In), % 0 to 0.1
0 to 0.1
Iron (Fe), % 0 to 0.020
0 to 0.020
Lead (Pb), % 38.5 to 40.3
35.9 to 38.5
Nickel (Ni), % 0 to 0.010
0 to 0.010
Silver (Ag), % 0 to 0.1
0 to 0.1
Tin (Sn), % 59.5 to 60.5
59.5 to 60.5
Zinc (Zn), % 0 to 0.0010
0 to 0.0010