Solder Alloy 134 vs. AWS ENiCrMo-3
Solder alloy 134 belongs to the otherwise unclassified metals classification, while AWS ENiCrMo-3 belongs to the nickel alloys.
For each property being compared, the top bar is solder alloy 134 and the bottom bar is AWS ENiCrMo-3.
Metric UnitsUS Customary Units
Mechanical Properties
| Elastic (Young's, Tensile) Modulus, GPa | 31 | |
| 200 |
| Elongation at Break, % | 31 | |
| 34 |
| Poisson's Ratio | 0.4 | |
| 0.29 |
| Shear Modulus, GPa | 11 | |
| 79 |
| Tensile Strength: Ultimate (UTS), MPa | 38 | |
| 870 |
Thermal Properties
| Latent Heat of Fusion, J/g | 41 | |
| 330 |
| Melting Completion (Liquidus), °C | 230 | |
| 1480 |
| Melting Onset (Solidus), °C | 190 | |
| 1430 |
| Specific Heat Capacity, J/kg-K | 170 | |
| 440 |
| Thermal Conductivity, W/m-K | 45 | |
| 11 |
| Thermal Expansion, µm/m-K | 26 | |
| 12 |
Electrical Properties
| Electrical Conductivity: Equal Volume, % IACS | 10 | |
| 1.3 |
| Electrical Conductivity: Equal Weight (Specific), % IACS | 9.6 | |
| 1.4 |
Otherwise Unclassified Properties
| Base Metal Price, % relative | 100 | |
| 80 |
| Density, g/cm3 | 9.6 | |
| 8.6 |
| Embodied Carbon, kg CO2/kg material | 8.5 | |
| 14 |
| Embodied Energy, MJ/kg | 140 | |
| 190 |
| Embodied Water, L/kg | 820 | |
| 290 |
Common Calculations
| Stiffness to Weight: Axial, points | 1.8 | |
| 13 |
| Stiffness to Weight: Bending, points | 11 | |
| 23 |
| Strength to Weight: Axial, points | 1.1 | |
| 28 |
| Strength to Weight: Bending, points | 2.6 | |
| 24 |
| Thermal Diffusivity, mm2/s | 28 | |
| 2.8 |
| Thermal Shock Resistance, points | 3.4 | |
| 25 |
Alloy Composition
Deprecated: Automatic conversion of false to array is deprecated in /home/public/compare.php on line 460
| Aluminum (Al), % | 0 to 0.0010 | |
| 0 |
| Antimony (Sb), % | 2.0 to 2.4 | |
| 0 |
| Arsenic (As), % | 0 to 0.030 | |
| 0 |
| Bismuth (Bi), % | 0 to 0.25 | |
| 0 |
| Cadmium (Cd), % | 0 to 0.0050 | |
| 0 |
| Carbon (C), % | 0 | |
| 0 to 0.1 |
| Chromium (Cr), % | 0 | |
| 20 to 23 |
| Cobalt (Co), % | 0 | |
| 0 to 0.12 |
| Copper (Cu), % | 0 to 0.080 | |
| 0 to 0.5 |
| Gold (Au), % | 0 to 0.050 | |
| 0 |
| Indium (In), % | 0 to 0.1 | |
| 0 |
| Iron (Fe), % | 0 to 0.020 | |
| 0 to 7.0 |
| Lead (Pb), % | 56.5 to 58.5 | |
| 0 |
| Manganese (Mn), % | 0 | |
| 0 to 1.0 |
| Molybdenum (Mo), % | 0 | |
| 8.0 to 10 |
| Nickel (Ni), % | 0 to 0.010 | |
| 55 to 68.9 |
| Niobium (Nb), % | 0 | |
| 3.2 to 4.2 |
| Phosphorus (P), % | 0 | |
| 0 to 0.030 |
| Silicon (Si), % | 0 | |
| 0 to 0.75 |
| Silver (Ag), % | 0 to 0.1 | |
| 0 |
| Sulfur (S), % | 0 | |
| 0 to 0.020 |
| Tin (Sn), % | 39.5 to 40.5 | |
| 0 |
| Zinc (Zn), % | 0 to 0.0010 | |
| 0 |
| Residuals, % | 0 | |
| 0 to 0.5 |