Solder Alloy 135 vs. AWS BAg-10
Both solder alloy 135 and AWS BAg-10 are otherwise unclassified metals. Both are furnished in the as-fabricated (no temper or treatment) condition. There are 15 material properties with values for both materials. Properties with values for just one material (10, in this case) are not shown.
For each property being compared, the top bar is solder alloy 135 and the bottom bar is AWS BAg-10.
Metric UnitsUS Customary Units
Mechanical Properties
| Elastic (Young's, Tensile) Modulus, GPa | 27 | |
| 82 |
| Poisson's Ratio | 0.41 | |
| 0.35 |
| Shear Modulus, GPa | 9.5 | |
| 30 |
| Tensile Strength: Ultimate (UTS), MPa | 35 | |
| 140 |
Thermal Properties
| Latent Heat of Fusion, J/g | 36 | |
| 130 |
| Melting Completion (Liquidus), °C | 250 | |
| 740 |
| Melting Onset (Solidus), °C | 190 | |
| 690 |
| Specific Heat Capacity, J/kg-K | 160 | |
| 280 |
| Thermal Expansion, µm/m-K | 27 | |
| 20 |
Otherwise Unclassified Properties
| Density, g/cm3 | 10 | |
| 9.8 |
Common Calculations
| Stiffness to Weight: Axial, points | 1.5 | |
| 4.6 |
| Stiffness to Weight: Bending, points | 9.9 | |
| 15 |
| Strength to Weight: Axial, points | 1.0 | |
| 4.0 |
| Strength to Weight: Bending, points | 2.4 | |
| 6.1 |
| Thermal Shock Resistance, points | 3.5 | |
| 6.2 |
Alloy Composition
Deprecated: Automatic conversion of false to array is deprecated in /home/public/compare.php on line 460
| Aluminum (Al), % | 0 to 0.0010 | |
| 0 |
| Antimony (Sb), % | 0.5 to 1.8 | |
| 0 |
| Arsenic (As), % | 0 to 0.030 | |
| 0 |
| Bismuth (Bi), % | 0 to 0.25 | |
| 0 |
| Cadmium (Cd), % | 0 to 0.0050 | |
| 0 |
| Copper (Cu), % | 0 to 0.080 | |
| 19 to 21 |
| Gold (Au), % | 0 to 0.050 | |
| 0 |
| Indium (In), % | 0 to 0.1 | |
| 0 |
| Iron (Fe), % | 0 to 0.020 | |
| 0 |
| Lead (Pb), % | 67.1 to 70 | |
| 0 |
| Nickel (Ni), % | 0 to 0.010 | |
| 0 |
| Silver (Ag), % | 0 to 0.1 | |
| 69 to 71 |
| Tin (Sn), % | 29.5 to 30.5 | |
| 0 |
| Zinc (Zn), % | 0 to 0.0010 | |
| 8.0 to 12 |
| Residuals, % | 0 | |
| 0 to 0.15 |