Solder Alloy 151 vs. EN 1.4749 Stainless Steel

Solder alloy 151 belongs to the otherwise unclassified metals classification, while EN 1.4749 stainless steel belongs to the iron alloys. There are 23 material properties with values for both materials. Properties with values for just one material (10, in this case) are not shown.

For each property being compared, the top bar is solder alloy 151 and the bottom bar is EN 1.4749 stainless steel.

Metric UnitsUS Customary Units

Mechanical Properties

Elastic (Young's, Tensile) Modulus, GPa 39
200
Elongation at Break, % 37
16
Poisson's Ratio 0.37
0.27
Shear Modulus, GPa 14
80
Tensile Strength: Ultimate (UTS), MPa 46
600

Thermal Properties

Latent Heat of Fusion, J/g 47
300
Melting Completion (Liquidus), °C 150
1420
Melting Onset (Solidus), °C 150
1380
Specific Heat Capacity, J/kg-K 190
490
Thermal Conductivity, W/m-K 44
17
Thermal Expansion, µm/m-K 26
9.6

Electrical Properties

Electrical Conductivity: Equal Volume, % IACS 10
2.5
Electrical Conductivity: Equal Weight (Specific), % IACS 10
2.9

Otherwise Unclassified Properties

Density, g/cm3 8.8
7.6
Embodied Carbon, kg CO2/kg material 9.2
2.5
Embodied Energy, MJ/kg 160
36
Embodied Water, L/kg 920
160

Common Calculations

Stiffness to Weight: Axial, points 2.5
15
Stiffness to Weight: Bending, points 13
26
Strength to Weight: Axial, points 1.4
22
Strength to Weight: Bending, points 3.2
21
Thermal Diffusivity, mm2/s 26
4.6
Thermal Shock Resistance, points 3.2
22

Alloy Composition

Aluminum (Al), % 0 to 0.0010
0
Antimony (Sb), % 0 to 0.2
0
Arsenic (As), % 0 to 0.030
0
Bismuth (Bi), % 0 to 0.1
0
Cadmium (Cd), % 17.5 to 18.5
0
Carbon (C), % 0
0.15 to 0.2
Chromium (Cr), % 0
26 to 29
Copper (Cu), % 0 to 0.080
0
Gold (Au), % 0 to 0.050
0
Indium (In), % 0 to 0.1
0
Iron (Fe), % 0 to 0.020
68.5 to 73.7
Lead (Pb), % 30.3 to 33
0
Manganese (Mn), % 0
0 to 1.0
Nickel (Ni), % 0 to 0.010
0
Nitrogen (N), % 0
0.15 to 0.25
Phosphorus (P), % 0
0 to 0.040
Silicon (Si), % 0
0 to 1.0
Silver (Ag), % 0 to 0.1
0
Sulfur (S), % 0
0 to 0.015
Tin (Sn), % 49.5 to 50.5
0
Zinc (Zn), % 0 to 0.0010
0