Solder Alloy 182 vs. EN 1.4646 Stainless Steel
Solder alloy 182 belongs to the otherwise unclassified metals classification, while EN 1.4646 stainless steel belongs to the iron alloys. There are 18 material properties with values for both materials. Properties with values for just one material (16, in this case) are not shown.
For each property being compared, the top bar is solder alloy 182 and the bottom bar is EN 1.4646 stainless steel.
Metric UnitsUS Customary Units
Mechanical Properties
| Elastic (Young's, Tensile) Modulus, GPa | 19 | |
| 200 |
| Elongation at Break, % | 37 | |
| 34 |
| Poisson's Ratio | 0.44 | |
| 0.28 |
| Shear Modulus, GPa | 6.7 | |
| 77 |
| Tensile Strength: Ultimate (UTS), MPa | 28 | |
| 750 |
Thermal Properties
| Latent Heat of Fusion, J/g | 28 | |
| 290 |
| Melting Completion (Liquidus), °C | 370 | |
| 1390 |
| Melting Onset (Solidus), °C | 300 | |
| 1340 |
| Specific Heat Capacity, J/kg-K | 130 | |
| 480 |
| Thermal Expansion, µm/m-K | 29 | |
| 17 |
Otherwise Unclassified Properties
| Density, g/cm3 | 11 | |
| 7.7 |
| Embodied Carbon, kg CO2/kg material | 9.0 | |
| 2.8 |
| Embodied Energy, MJ/kg | 140 | |
| 41 |
Common Calculations
| Stiffness to Weight: Axial, points | 0.95 | |
| 14 |
| Stiffness to Weight: Bending, points | 7.9 | |
| 25 |
| Strength to Weight: Axial, points | 0.69 | |
| 27 |
| Strength to Weight: Bending, points | 1.8 | |
| 24 |
| Thermal Shock Resistance, points | 3.7 | |
| 16 |
Alloy Composition
| Aluminum (Al), % | 0 to 0.0010 | |
| 0 |
| Antimony (Sb), % | 0 to 0.2 | |
| 0 |
| Arsenic (As), % | 0 to 0.030 | |
| 0 |
| Bismuth (Bi), % | 0 to 0.1 | |
| 0 |
| Cadmium (Cd), % | 0 to 0.0020 | |
| 0 |
| Carbon (C), % | 0 | |
| 0.020 to 0.1 |
| Chromium (Cr), % | 0 | |
| 17 to 19 |
| Copper (Cu), % | 0 to 0.080 | |
| 1.5 to 3.0 |
| Gold (Au), % | 0 to 0.050 | |
| 0 |
| Indium (In), % | 0 to 0.1 | |
| 0 |
| Iron (Fe), % | 0 to 0.020 | |
| 59 to 67.3 |
| Lead (Pb), % | 93.2 to 95 | |
| 0 |
| Manganese (Mn), % | 0 | |
| 10.5 to 12.5 |
| Molybdenum (Mo), % | 0 | |
| 0 to 0.5 |
| Nickel (Ni), % | 0 to 0.010 | |
| 3.5 to 4.5 |
| Nitrogen (N), % | 0 | |
| 0.2 to 0.3 |
| Phosphorus (P), % | 0 | |
| 0 to 0.050 |
| Silicon (Si), % | 0 | |
| 0 to 1.0 |
| Silver (Ag), % | 5.0 to 6.0 | |
| 0 |
| Sulfur (S), % | 0 | |
| 0 to 0.015 |
| Tin (Sn), % | 0 to 0.25 | |
| 0 |
| Zinc (Zn), % | 0 to 0.0010 | |
| 0 |