Solder Alloy 182 vs. Grade 1 Babbitt Metal

Both solder alloy 182 and grade 1 Babbitt Metal are otherwise unclassified metals. Both are furnished in the as-fabricated (no temper or treatment) condition. There are 18 material properties with values for both materials. Properties with values for just one material (10, in this case) are not shown.

For each property being compared, the top bar is solder alloy 182 and the bottom bar is grade 1 Babbitt Metal.

Metric UnitsUS Customary Units

Mechanical Properties

Elastic (Young's, Tensile) Modulus, GPa 19
53
Elongation at Break, % 37
34
Poisson's Ratio 0.44
0.35
Shear Modulus, GPa 6.7
20

Thermal Properties

Latent Heat of Fusion, J/g 28
70
Melting Completion (Liquidus), °C 370
370
Melting Onset (Solidus), °C 300
220
Specific Heat Capacity, J/kg-K 130
230
Thermal Conductivity, W/m-K 27
45
Thermal Expansion, µm/m-K 29
21

Electrical Properties

Electrical Conductivity: Equal Volume, % IACS 9.6
13
Electrical Conductivity: Equal Weight (Specific), % IACS 7.6
16

Otherwise Unclassified Properties

Density, g/cm3 11
7.3
Embodied Carbon, kg CO2/kg material 9.0
12
Embodied Energy, MJ/kg 140
200

Common Calculations

Stiffness to Weight: Axial, points 0.95
4.0
Stiffness to Weight: Bending, points 7.9
17
Thermal Diffusivity, mm2/s 18
26

Alloy Composition

Aluminum (Al), % 0 to 0.0010
0 to 0.0050
Antimony (Sb), % 0 to 0.2
4.0 to 5.0
Arsenic (As), % 0 to 0.030
0 to 0.1
Bismuth (Bi), % 0 to 0.1
0 to 0.080
Cadmium (Cd), % 0 to 0.0020
0 to 0.050
Copper (Cu), % 0 to 0.080
4.0 to 5.0
Gold (Au), % 0 to 0.050
0
Indium (In), % 0 to 0.1
0
Iron (Fe), % 0 to 0.020
0 to 0.080
Lead (Pb), % 93.2 to 95
0 to 0.35
Nickel (Ni), % 0 to 0.010
0
Silver (Ag), % 5.0 to 6.0
0
Tin (Sn), % 0 to 0.25
89.3 to 92
Zinc (Zn), % 0 to 0.0010
0 to 0.0050