Solder Alloy 182 vs. Grade 250 Maraging Steel
Solder alloy 182 belongs to the otherwise unclassified metals classification, while grade 250 maraging steel belongs to the iron alloys. There are 18 material properties with values for both materials. Properties with values for just one material (12, in this case) are not shown.
For each property being compared, the top bar is solder alloy 182 and the bottom bar is grade 250 maraging steel.
Metric UnitsUS Customary Units
Mechanical Properties
| Elastic (Young's, Tensile) Modulus, GPa | 19 | |
| 190 |
| Elongation at Break, % | 37 | |
| 7.3 to 17 |
| Poisson's Ratio | 0.44 | |
| 0.3 |
| Shear Modulus, GPa | 6.7 | |
| 75 |
| Tensile Strength: Ultimate (UTS), MPa | 28 | |
| 970 to 1800 |
Thermal Properties
| Latent Heat of Fusion, J/g | 28 | |
| 270 |
| Melting Completion (Liquidus), °C | 370 | |
| 1480 |
| Melting Onset (Solidus), °C | 300 | |
| 1430 |
| Specific Heat Capacity, J/kg-K | 130 | |
| 450 |
| Thermal Expansion, µm/m-K | 29 | |
| 12 |
Otherwise Unclassified Properties
| Density, g/cm3 | 11 | |
| 8.2 |
| Embodied Carbon, kg CO2/kg material | 9.0 | |
| 4.9 |
| Embodied Energy, MJ/kg | 140 | |
| 65 |
Common Calculations
| Stiffness to Weight: Axial, points | 0.95 | |
| 13 |
| Stiffness to Weight: Bending, points | 7.9 | |
| 23 |
| Strength to Weight: Axial, points | 0.69 | |
| 33 to 61 |
| Strength to Weight: Bending, points | 1.8 | |
| 26 to 40 |
| Thermal Shock Resistance, points | 3.7 | |
| 29 to 54 |
Alloy Composition
| Aluminum (Al), % | 0 to 0.0010 | |
| 0.050 to 0.15 |
| Antimony (Sb), % | 0 to 0.2 | |
| 0 |
| Arsenic (As), % | 0 to 0.030 | |
| 0 |
| Bismuth (Bi), % | 0 to 0.1 | |
| 0 |
| Boron (B), % | 0 | |
| 0 to 0.0030 |
| Cadmium (Cd), % | 0 to 0.0020 | |
| 0 |
| Calcium (Ca), % | 0 | |
| 0 to 0.050 |
| Carbon (C), % | 0 | |
| 0 to 0.030 |
| Cobalt (Co), % | 0 | |
| 7.0 to 8.5 |
| Copper (Cu), % | 0 to 0.080 | |
| 0 |
| Gold (Au), % | 0 to 0.050 | |
| 0 |
| Indium (In), % | 0 to 0.1 | |
| 0 |
| Iron (Fe), % | 0 to 0.020 | |
| 66.3 to 71.1 |
| Lead (Pb), % | 93.2 to 95 | |
| 0 |
| Manganese (Mn), % | 0 | |
| 0 to 0.1 |
| Molybdenum (Mo), % | 0 | |
| 4.6 to 5.2 |
| Nickel (Ni), % | 0 to 0.010 | |
| 17 to 19 |
| Phosphorus (P), % | 0 | |
| 0 to 0.010 |
| Silicon (Si), % | 0 | |
| 0 to 0.1 |
| Silver (Ag), % | 5.0 to 6.0 | |
| 0 |
| Sulfur (S), % | 0 | |
| 0 to 0.010 |
| Tin (Sn), % | 0 to 0.25 | |
| 0 |
| Titanium (Ti), % | 0 | |
| 0.3 to 0.5 |
| Zinc (Zn), % | 0 to 0.0010 | |
| 0 |
| Zirconium (Zr), % | 0 | |
| 0 to 0.020 |