Solder Alloy 191 vs. CC496K Bronze
Solder alloy 191 belongs to the otherwise unclassified metals classification, while CC496K bronze belongs to the copper alloys. They have a modest 20% of their average alloy composition in common, which, by itself, doesn't mean much. There are 22 material properties with values for both materials. Properties with values for just one material (7, in this case) are not shown.
For each property being compared, the top bar is solder alloy 191 and the bottom bar is CC496K bronze.
Metric UnitsUS Customary Units
Mechanical Properties
| Elastic (Young's, Tensile) Modulus, GPa | 19 | |
| 97 |
| Elongation at Break, % | 32 | |
| 8.6 |
| Poisson's Ratio | 0.43 | |
| 0.35 |
| Shear Modulus, GPa | 6.5 | |
| 36 |
| Tensile Strength: Ultimate (UTS), MPa | 29 | |
| 210 |
Thermal Properties
| Latent Heat of Fusion, J/g | 27 | |
| 170 |
| Melting Completion (Liquidus), °C | 300 | |
| 900 |
| Melting Onset (Solidus), °C | 300 | |
| 820 |
| Specific Heat Capacity, J/kg-K | 130 | |
| 340 |
| Thermal Conductivity, W/m-K | 24 | |
| 52 |
| Thermal Expansion, µm/m-K | 29 | |
| 19 |
Electrical Properties
| Electrical Conductivity: Equal Volume, % IACS | 8.8 | |
| 11 |
| Electrical Conductivity: Equal Weight (Specific), % IACS | 7.2 | |
| 11 |
Otherwise Unclassified Properties
| Density, g/cm3 | 11 | |
| 9.2 |
| Embodied Carbon, kg CO2/kg material | 5.8 | |
| 3.3 |
| Embodied Energy, MJ/kg | 95 | |
| 52 |
Common Calculations
| Stiffness to Weight: Axial, points | 0.93 | |
| 5.9 |
| Stiffness to Weight: Bending, points | 8.0 | |
| 17 |
| Strength to Weight: Axial, points | 0.72 | |
| 6.5 |
| Strength to Weight: Bending, points | 1.9 | |
| 8.6 |
| Thermal Diffusivity, mm2/s | 16 | |
| 17 |
| Thermal Shock Resistance, points | 3.9 | |
| 8.1 |
Alloy Composition
| Aluminum (Al), % | 0 to 0.0010 | |
| 0 to 0.010 |
| Antimony (Sb), % | 0 to 0.2 | |
| 0 to 0.5 |
| Arsenic (As), % | 0 to 0.030 | |
| 0 |
| Bismuth (Bi), % | 0 to 0.1 | |
| 0 |
| Cadmium (Cd), % | 0 to 0.0020 | |
| 0 |
| Copper (Cu), % | 0 to 0.080 | |
| 72 to 79.5 |
| Gold (Au), % | 0 to 0.050 | |
| 0 |
| Indium (In), % | 0 to 0.1 | |
| 0 |
| Iron (Fe), % | 0 to 0.020 | |
| 0 to 0.25 |
| Lead (Pb), % | 92.4 to 94 | |
| 13 to 17 |
| Manganese (Mn), % | 0 | |
| 0 to 0.2 |
| Nickel (Ni), % | 0 to 0.010 | |
| 0.5 to 2.0 |
| Phosphorus (P), % | 0 | |
| 0 to 0.1 |
| Silicon (Si), % | 0 | |
| 0 to 0.010 |
| Silver (Ag), % | 1.2 to 1.8 | |
| 0 |
| Sulfur (S), % | 0 | |
| 0 to 0.1 |
| Tin (Sn), % | 4.8 to 5.2 | |
| 6.0 to 8.0 |
| Zinc (Zn), % | 0 to 0.0010 | |
| 0 to 2.0 |