Solder Alloy 201 vs. Solder Alloy 131

Both solder alloy 201 and solder alloy 131 are otherwise unclassified metals. Both are furnished in the as-fabricated (no temper or treatment) condition. They have 64% of their average alloy composition in common. There are 23 material properties with values for both materials. Properties with values for just one material (1, in this case) are not shown.

For each property being compared, the top bar is solder alloy 201 and the bottom bar is solder alloy 131.

Metric UnitsUS Customary Units

Mechanical Properties

Elastic (Young's, Tensile) Modulus, GPa 50
38
Elongation at Break, % 38
47
Poisson's Ratio 0.35
0.39
Shear Modulus, GPa 19
14
Tensile Strength: Ultimate (UTS), MPa 41
31

Thermal Properties

Latent Heat of Fusion, J/g 64
46
Melting Completion (Liquidus), °C 240
180
Melting Onset (Solidus), °C 240
180
Specific Heat Capacity, J/kg-K 220
190
Thermal Conductivity, W/m-K 28
55
Thermal Expansion, µm/m-K 21
25

Electrical Properties

Electrical Conductivity: Equal Volume, % IACS 12
11
Electrical Conductivity: Equal Weight (Specific), % IACS 15
12

Otherwise Unclassified Properties

Density, g/cm3 7.3
8.8
Embodied Carbon, kg CO2/kg material 15
11
Embodied Energy, MJ/kg 250
180
Embodied Water, L/kg 1320
940

Common Calculations

Stiffness to Weight: Axial, points 3.8
2.4
Stiffness to Weight: Bending, points 17
13
Strength to Weight: Axial, points 1.6
1.0
Strength to Weight: Bending, points 3.6
2.5
Thermal Diffusivity, mm2/s 17
33
Thermal Shock Resistance, points 2.7
2.4

Alloy Composition

Aluminum (Al), % 0 to 0.0010
0 to 0.0010
Antimony (Sb), % 4.5 to 5.5
0.2 to 0.5
Arsenic (As), % 0 to 0.030
0 to 0.030
Bismuth (Bi), % 0 to 0.1
0 to 0.1
Cadmium (Cd), % 0 to 0.0020
0 to 0.0020
Copper (Cu), % 0 to 0.050
0 to 0.080
Gold (Au), % 0 to 0.050
0 to 0.050
Indium (In), % 0 to 0.1
0 to 0.1
Iron (Fe), % 0 to 0.020
0 to 0.020
Lead (Pb), % 0 to 0.070
35.5 to 37.3
Nickel (Ni), % 0 to 0.010
0 to 0.010
Silver (Ag), % 0 to 0.1
0 to 0.1
Tin (Sn), % 94 to 95.5
62.5 to 63.5
Zinc (Zn), % 0 to 0.0010
0 to 0.0010