Solder Alloy 301 vs. ASTM B817 Type I
Solder alloy 301 belongs to the otherwise unclassified metals classification, while ASTM B817 type I belongs to the titanium alloys. There are 25 material properties with values for both materials. Properties with values for just one material (6, in this case) are not shown.
For each property being compared, the top bar is solder alloy 301 and the bottom bar is ASTM B817 type I.
Metric UnitsUS Customary Units
Mechanical Properties
| Elastic (Young's, Tensile) Modulus, GPa | 40 | |
| 100 |
| Elongation at Break, % | 51 | |
| 4.0 to 13 |
| Poisson's Ratio | 0.34 | |
| 0.32 |
| Shear Modulus, GPa | 15 | |
| 40 |
| Tensile Strength: Ultimate (UTS), MPa | 55 | |
| 770 to 960 |
| Tensile Strength: Yield (Proof), MPa | 49 | |
| 700 to 860 |
Thermal Properties
| Latent Heat of Fusion, J/g | 55 | |
| 410 |
| Melting Completion (Liquidus), °C | 140 | |
| 1600 |
| Melting Onset (Solidus), °C | 140 | |
| 1550 |
| Specific Heat Capacity, J/kg-K | 160 | |
| 560 |
| Thermal Conductivity, W/m-K | 19 | |
| 7.1 |
| Thermal Expansion, µm/m-K | 14 | |
| 9.6 |
Electrical Properties
| Electrical Conductivity: Equal Volume, % IACS | 4.7 | |
| 1.0 |
| Electrical Conductivity: Equal Weight (Specific), % IACS | 4.9 | |
| 2.0 |
Otherwise Unclassified Properties
| Density, g/cm3 | 8.7 | |
| 4.4 |
| Embodied Carbon, kg CO2/kg material | 13 | |
| 38 |
| Embodied Energy, MJ/kg | 210 | |
| 610 |
Common Calculations
| Resilience: Ultimate (Unit Rupture Work), MJ/m3 | 27 | |
| 30 to 120 |
| Resilience: Unit (Modulus of Resilience), kJ/m3 | 30 | |
| 2310 to 3540 |
| Stiffness to Weight: Axial, points | 2.5 | |
| 13 |
| Stiffness to Weight: Bending, points | 13 | |
| 35 |
| Strength to Weight: Axial, points | 1.8 | |
| 48 to 60 |
| Strength to Weight: Bending, points | 3.7 | |
| 42 to 49 |
| Thermal Diffusivity, mm2/s | 13 | |
| 2.9 |
| Thermal Shock Resistance, points | 7.2 | |
| 54 to 68 |
Alloy Composition
Deprecated: Automatic conversion of false to array is deprecated in /home/public/compare.php on line 460
| Aluminum (Al), % | 0 to 0.0010 | |
| 5.5 to 6.8 |
| Antimony (Sb), % | 0 to 0.1 | |
| 0 |
| Arsenic (As), % | 0 to 0.030 | |
| 0 |
| Bismuth (Bi), % | 56.5 to 59 | |
| 0 |
| Cadmium (Cd), % | 0 to 0.0020 | |
| 0 |
| Carbon (C), % | 0 | |
| 0 to 0.1 |
| Chlorine (Cl), % | 0 | |
| 0 to 0.2 |
| Copper (Cu), % | 0 to 0.050 | |
| 0 |
| Gold (Au), % | 0 to 0.050 | |
| 0 |
| Hydrogen (H), % | 0 | |
| 0 to 0.015 |
| Indium (In), % | 0 to 0.1 | |
| 0 |
| Iron (Fe), % | 0 to 0.020 | |
| 0 to 0.4 |
| Lead (Pb), % | 0 to 0.070 | |
| 0 |
| Nickel (Ni), % | 0 to 0.010 | |
| 0 |
| Nitrogen (N), % | 0 | |
| 0 to 0.040 |
| Oxygen (O), % | 0 | |
| 0 to 0.3 |
| Silicon (Si), % | 0 | |
| 0 to 0.1 |
| Silver (Ag), % | 0 to 0.1 | |
| 0 |
| Sodium (Na), % | 0 | |
| 0 to 0.2 |
| Tin (Sn), % | 41 to 43 | |
| 0 |
| Titanium (Ti), % | 0 | |
| 87 to 91 |
| Vanadium (V), % | 0 | |
| 3.5 to 4.5 |
| Zinc (Zn), % | 0 to 0.0010 | |
| 0 |
| Residuals, % | 0 | |
| 0 to 0.4 |