Solder Alloy 401 vs. Z13004 Zinc
Solder alloy 401 belongs to the otherwise unclassified metals classification, while Z13004 zinc belongs to the zinc alloys. There are 23 material properties with values for both materials. Properties with values for just one material (6, in this case) are not shown.
For each property being compared, the top bar is solder alloy 401 and the bottom bar is Z13004 zinc.
Metric UnitsUS Customary Units
Mechanical Properties
Elastic (Young's, Tensile) Modulus, GPa | 50 | |
87 |
Elongation at Break, % | 21 | |
30 |
Poisson's Ratio | 0.36 | |
0.25 |
Shear Modulus, GPa | 19 | |
35 |
Tensile Strength: Ultimate (UTS), MPa | 29 | |
93 |
Thermal Properties
Latent Heat of Fusion, J/g | 60 | |
110 |
Melting Completion (Liquidus), °C | 230 | |
410 |
Melting Onset (Solidus), °C | 230 | |
390 |
Specific Heat Capacity, J/kg-K | 220 | |
390 |
Thermal Conductivity, W/m-K | 66 | |
110 |
Thermal Expansion, µm/m-K | 22 | |
26 |
Electrical Properties
Electrical Conductivity: Equal Volume, % IACS | 14 | |
27 |
Electrical Conductivity: Equal Weight (Specific), % IACS | 17 | |
37 |
Otherwise Unclassified Properties
Density, g/cm3 | 7.3 | |
6.6 |
Embodied Carbon, kg CO2/kg material | 15 | |
2.8 |
Embodied Energy, MJ/kg | 250 | |
53 |
Embodied Water, L/kg | 1200 | |
340 |
Common Calculations
Stiffness to Weight: Axial, points | 3.8 | |
7.4 |
Stiffness to Weight: Bending, points | 17 | |
23 |
Strength to Weight: Axial, points | 1.1 | |
3.9 |
Strength to Weight: Bending, points | 2.9 | |
7.0 |
Thermal Diffusivity, mm2/s | 40 | |
44 |
Thermal Shock Resistance, points | 1.9 | |
2.9 |
Alloy Composition
Aluminum (Al), % | 0 to 0.0010 | |
0 to 0.0020 |
Antimony (Sb), % | 0 to 0.1 | |
0 |
Arsenic (As), % | 0 to 0.030 | |
0 |
Bismuth (Bi), % | 0 to 0.1 | |
0 |
Cadmium (Cd), % | 0 to 0.0020 | |
0 to 0.0030 |
Copper (Cu), % | 0.5 to 0.9 | |
0 to 0.0030 |
Gold (Au), % | 0 to 0.050 | |
0 |
Indium (In), % | 0 to 0.1 | |
0 |
Iron (Fe), % | 0 to 0.020 | |
0 to 0.0030 |
Lead (Pb), % | 0 to 0.070 | |
0 to 0.0030 |
Nickel (Ni), % | 0 to 0.010 | |
0 |
Silver (Ag), % | 0 to 0.1 | |
0 |
Tin (Sn), % | 98.5 to 99.5 | |
0 to 0.0010 |
Zinc (Zn), % | 0 to 0.0010 | |
99.985 to 100 |