Solder Alloy 702 vs. R30016 Cobalt

Solder alloy 702 belongs to the otherwise unclassified metals classification, while R30016 cobalt belongs to the cobalt alloys. There are 22 material properties with values for both materials. Properties with values for just one material (10, in this case) are not shown.

For each property being compared, the top bar is solder alloy 702 and the bottom bar is R30016 cobalt.

Metric UnitsUS Customary Units

Mechanical Properties

Elastic (Young's, Tensile) Modulus, GPa 51
220
Elongation at Break, % 21
8.4
Poisson's Ratio 0.36
0.28
Shear Modulus, GPa 19
85
Tensile Strength: Ultimate (UTS), MPa 53
1010

Thermal Properties

Latent Heat of Fusion, J/g 61
320
Melting Completion (Liquidus), °C 220
1360
Melting Onset (Solidus), °C 220
1270
Specific Heat Capacity, J/kg-K 220
450
Thermal Conductivity, W/m-K 62
15
Thermal Expansion, µm/m-K 22
14

Electrical Properties

Electrical Conductivity: Equal Volume, % IACS 15
1.9
Electrical Conductivity: Equal Weight (Specific), % IACS 18
2.0

Otherwise Unclassified Properties

Density, g/cm3 7.4
8.5
Embodied Carbon, kg CO2/kg material 17
7.7
Embodied Energy, MJ/kg 290
110

Common Calculations

Stiffness to Weight: Axial, points 3.8
14
Stiffness to Weight: Bending, points 17
24
Strength to Weight: Axial, points 2.0
33
Strength to Weight: Bending, points 4.2
26
Thermal Diffusivity, mm2/s 38
3.9
Thermal Shock Resistance, points 3.4
24

Alloy Composition

Aluminum (Al), % 0 to 0.0010
0
Antimony (Sb), % 0 to 0.1
0
Arsenic (As), % 0 to 0.030
0
Bismuth (Bi), % 0 to 0.1
0
Cadmium (Cd), % 0 to 0.0020
0
Carbon (C), % 0
0.9 to 1.4
Chromium (Cr), % 0
28 to 32
Cobalt (Co), % 0
49.6 to 66.9
Copper (Cu), % 0 to 0.050
0
Gold (Au), % 0 to 0.050
0
Indium (In), % 0 to 0.1
0
Iron (Fe), % 0 to 0.020
0 to 3.0
Lead (Pb), % 0 to 0.070
0
Manganese (Mn), % 0
0.5 to 2.0
Molybdenum (Mo), % 0
0 to 1.5
Nickel (Ni), % 0 to 0.010
0 to 3.0
Silicon (Si), % 0
0.2 to 2.0
Silver (Ag), % 2.8 to 3.2
0
Tin (Sn), % 96.3 to 97.2
0
Tungsten (W), % 0
3.5 to 5.5
Zinc (Zn), % 0 to 0.0010
0