Solder Alloy 715 vs. CC212E Bronze
Solder alloy 715 belongs to the otherwise unclassified metals classification, while CC212E bronze belongs to the copper alloys. There are 21 material properties with values for both materials. Properties with values for just one material (8, in this case) are not shown.
For each property being compared, the top bar is solder alloy 715 and the bottom bar is CC212E bronze.
Metric UnitsUS Customary Units
Mechanical Properties
| Brinell Hardness | 16 | |
| 170 |
| Elastic (Young's, Tensile) Modulus, GPa | 51 | |
| 130 |
| Elongation at Break, % | 21 | |
| 20 |
| Poisson's Ratio | 0.36 | |
| 0.34 |
| Shear Modulus, GPa | 19 | |
| 47 |
| Tensile Strength: Ultimate (UTS), MPa | 30 | |
| 710 |
Thermal Properties
| Latent Heat of Fusion, J/g | 61 | |
| 230 |
| Melting Completion (Liquidus), °C | 220 | |
| 1080 |
| Melting Onset (Solidus), °C | 220 | |
| 1020 |
| Specific Heat Capacity, J/kg-K | 220 | |
| 440 |
| Thermal Expansion, µm/m-K | 22 | |
| 18 |
Electrical Properties
| Electrical Conductivity: Equal Volume, % IACS | 12 | |
| 3.0 |
| Electrical Conductivity: Equal Weight (Specific), % IACS | 15 | |
| 3.3 |
Otherwise Unclassified Properties
| Density, g/cm3 | 7.3 | |
| 8.2 |
| Embodied Carbon, kg CO2/kg material | 16 | |
| 3.4 |
| Embodied Energy, MJ/kg | 270 | |
| 55 |
Common Calculations
| Stiffness to Weight: Axial, points | 3.8 | |
| 8.5 |
| Stiffness to Weight: Bending, points | 17 | |
| 20 |
| Strength to Weight: Axial, points | 1.1 | |
| 24 |
| Strength to Weight: Bending, points | 2.9 | |
| 21 |
| Thermal Shock Resistance, points | 1.9 | |
| 22 |
Alloy Composition
| Aluminum (Al), % | 0 to 0.0010 | |
| 7.0 to 9.0 |
| Antimony (Sb), % | 0 to 0.1 | |
| 0 |
| Arsenic (As), % | 0 to 0.030 | |
| 0 |
| Bismuth (Bi), % | 0 to 0.1 | |
| 0 |
| Cadmium (Cd), % | 0 to 0.0020 | |
| 0 |
| Copper (Cu), % | 0.5 to 0.9 | |
| 68 to 77 |
| Gold (Au), % | 0 to 0.050 | |
| 0 |
| Indium (In), % | 0 to 0.1 | |
| 0 |
| Iron (Fe), % | 0 to 0.020 | |
| 2.0 to 4.0 |
| Lead (Pb), % | 0 to 0.070 | |
| 0 to 0.050 |
| Magnesium (Mg), % | 0 | |
| 0 to 0.050 |
| Manganese (Mn), % | 0 | |
| 8.0 to 15 |
| Nickel (Ni), % | 0 to 0.010 | |
| 1.5 to 4.5 |
| Silicon (Si), % | 0 | |
| 0 to 0.1 |
| Silver (Ag), % | 0.8 to 1.2 | |
| 0 |
| Tin (Sn), % | 97.4 to 98.7 | |
| 0 to 0.5 |
| Zinc (Zn), % | 0 to 0.0010 | |
| 0 to 1.0 |