Solder Alloy 715 vs. CC753S Brass

Solder alloy 715 belongs to the otherwise unclassified metals classification, while CC753S brass belongs to the copper alloys. There are 23 material properties with values for both materials. Properties with values for just one material (6, in this case) are not shown.

For each property being compared, the top bar is solder alloy 715 and the bottom bar is CC753S brass.

Metric UnitsUS Customary Units

Mechanical Properties

Brinell Hardness 16
100
Elastic (Young's, Tensile) Modulus, GPa 51
100
Elongation at Break, % 21
17
Poisson's Ratio 0.36
0.31
Shear Modulus, GPa 19
40
Tensile Strength: Ultimate (UTS), MPa 30
340

Thermal Properties

Latent Heat of Fusion, J/g 61
170
Melting Completion (Liquidus), °C 220
820
Melting Onset (Solidus), °C 220
780
Specific Heat Capacity, J/kg-K 220
390
Thermal Conductivity, W/m-K 60
99
Thermal Expansion, µm/m-K 22
21

Electrical Properties

Electrical Conductivity: Equal Volume, % IACS 12
26
Electrical Conductivity: Equal Weight (Specific), % IACS 15
29

Otherwise Unclassified Properties

Density, g/cm3 7.3
8.1
Embodied Carbon, kg CO2/kg material 16
2.8
Embodied Energy, MJ/kg 270
47

Common Calculations

Stiffness to Weight: Axial, points 3.8
7.1
Stiffness to Weight: Bending, points 17
19
Strength to Weight: Axial, points 1.1
12
Strength to Weight: Bending, points 2.9
13
Thermal Diffusivity, mm2/s 37
32
Thermal Shock Resistance, points 1.9
11

Alloy Composition

Aluminum (Al), % 0 to 0.0010
0.4 to 0.8
Antimony (Sb), % 0 to 0.1
0 to 0.050
Arsenic (As), % 0 to 0.030
0
Bismuth (Bi), % 0 to 0.1
0
Cadmium (Cd), % 0 to 0.0020
0
Copper (Cu), % 0.5 to 0.9
56.8 to 60.5
Gold (Au), % 0 to 0.050
0
Indium (In), % 0 to 0.1
0
Iron (Fe), % 0 to 0.020
0.5 to 0.8
Lead (Pb), % 0 to 0.070
1.8 to 2.5
Manganese (Mn), % 0
0 to 0.2
Nickel (Ni), % 0 to 0.010
0.5 to 1.2
Phosphorus (P), % 0
0 to 0.020
Silicon (Si), % 0
0 to 0.050
Silver (Ag), % 0.8 to 1.2
0
Tin (Sn), % 97.4 to 98.7
0 to 0.8
Zinc (Zn), % 0 to 0.0010
33.1 to 40