MakeItFrom.com
Menu (ESC)

Solder Alloy 715 vs. C14180 Copper

Solder alloy 715 belongs to the otherwise unclassified metals classification, while C14180 copper belongs to the copper alloys. There are 20 material properties with values for both materials. Properties with values for just one material (10, in this case) are not shown.

For each property being compared, the top bar is solder alloy 715 and the bottom bar is C14180 copper.

Metric UnitsUS Customary Units

Mechanical Properties

Elastic (Young's, Tensile) Modulus, GPa 51
120
Elongation at Break, % 21
15
Poisson's Ratio 0.36
0.34
Shear Modulus, GPa 19
43
Tensile Strength: Ultimate (UTS), MPa 30
210

Thermal Properties

Latent Heat of Fusion, J/g 61
210
Melting Completion (Liquidus), °C 220
1080
Melting Onset (Solidus), °C 220
1080
Specific Heat Capacity, J/kg-K 220
390
Thermal Conductivity, W/m-K 60
370
Thermal Expansion, µm/m-K 22
17

Otherwise Unclassified Properties

Density, g/cm3 7.3
9.0
Embodied Carbon, kg CO2/kg material 16
2.6
Embodied Energy, MJ/kg 270
41

Common Calculations

Stiffness to Weight: Axial, points 3.8
7.2
Stiffness to Weight: Bending, points 17
18
Strength to Weight: Axial, points 1.1
6.5
Strength to Weight: Bending, points 2.9
8.8
Thermal Diffusivity, mm2/s 37
110
Thermal Shock Resistance, points 1.9
7.4

Alloy Composition

Aluminum (Al), % 0 to 0.0010
0 to 0.010
Antimony (Sb), % 0 to 0.1
0
Arsenic (As), % 0 to 0.030
0
Bismuth (Bi), % 0 to 0.1
0
Cadmium (Cd), % 0 to 0.0020
0
Copper (Cu), % 0.5 to 0.9
99.9 to 100
Gold (Au), % 0 to 0.050
0
Indium (In), % 0 to 0.1
0
Iron (Fe), % 0 to 0.020
0
Lead (Pb), % 0 to 0.070
0 to 0.020
Nickel (Ni), % 0 to 0.010
0
Phosphorus (P), % 0
0 to 0.075
Silver (Ag), % 0.8 to 1.2
0
Tin (Sn), % 97.4 to 98.7
0
Zinc (Zn), % 0 to 0.0010
0