Solder Alloy 715 vs. C84000 Brass

Solder alloy 715 belongs to the otherwise unclassified metals classification, while C84000 brass belongs to the copper alloys. There are 23 material properties with values for both materials. Properties with values for just one material (6, in this case) are not shown.

For each property being compared, the top bar is solder alloy 715 and the bottom bar is C84000 brass.

Metric UnitsUS Customary Units

Mechanical Properties

Brinell Hardness 16
65
Elastic (Young's, Tensile) Modulus, GPa 51
110
Elongation at Break, % 21
27
Poisson's Ratio 0.36
0.33
Shear Modulus, GPa 19
42
Tensile Strength: Ultimate (UTS), MPa 30
250

Thermal Properties

Latent Heat of Fusion, J/g 61
190
Melting Completion (Liquidus), °C 220
1040
Melting Onset (Solidus), °C 220
940
Specific Heat Capacity, J/kg-K 220
380
Thermal Conductivity, W/m-K 60
72
Thermal Expansion, µm/m-K 22
18

Electrical Properties

Electrical Conductivity: Equal Volume, % IACS 12
16
Electrical Conductivity: Equal Weight (Specific), % IACS 15
17

Otherwise Unclassified Properties

Density, g/cm3 7.3
8.6
Embodied Carbon, kg CO2/kg material 16
3.0
Embodied Energy, MJ/kg 270
49

Common Calculations

Stiffness to Weight: Axial, points 3.8
7.2
Stiffness to Weight: Bending, points 17
19
Strength to Weight: Axial, points 1.1
8.2
Strength to Weight: Bending, points 2.9
10
Thermal Diffusivity, mm2/s 37
22
Thermal Shock Resistance, points 1.9
9.0

Alloy Composition


Deprecated: Automatic conversion of false to array is deprecated in /home/public/compare.php on line 460
Aluminum (Al), % 0 to 0.0010
0 to 0.0050
Antimony (Sb), % 0 to 0.1
0 to 0.020
Arsenic (As), % 0 to 0.030
0
Bismuth (Bi), % 0 to 0.1
0
Boron (B), % 0
0 to 0.1
Cadmium (Cd), % 0 to 0.0020
0
Copper (Cu), % 0.5 to 0.9
82 to 89
Gold (Au), % 0 to 0.050
0
Indium (In), % 0 to 0.1
0
Iron (Fe), % 0 to 0.020
0 to 0.4
Lead (Pb), % 0 to 0.070
0 to 0.090
Manganese (Mn), % 0
0 to 0.010
Nickel (Ni), % 0 to 0.010
0.5 to 2.0
Phosphorus (P), % 0
0 to 0.050
Silicon (Si), % 0
0 to 0.0050
Silver (Ag), % 0.8 to 1.2
0
Sulfur (S), % 0
0.1 to 0.65
Tin (Sn), % 97.4 to 98.7
2.0 to 4.0
Zinc (Zn), % 0 to 0.0010
5.0 to 14
Zirconium (Zr), % 0
0 to 0.1
Residuals, % 0
0 to 0.7