Solder Alloy 715 vs. C90200 Bronze

Solder alloy 715 belongs to the otherwise unclassified metals classification, while C90200 bronze belongs to the copper alloys. There are 23 material properties with values for both materials. Properties with values for just one material (6, in this case) are not shown.

For each property being compared, the top bar is solder alloy 715 and the bottom bar is C90200 bronze.

Metric UnitsUS Customary Units

Mechanical Properties

Brinell Hardness 16
70
Elastic (Young's, Tensile) Modulus, GPa 51
110
Elongation at Break, % 21
30
Poisson's Ratio 0.36
0.34
Shear Modulus, GPa 19
41
Tensile Strength: Ultimate (UTS), MPa 30
260

Thermal Properties

Latent Heat of Fusion, J/g 61
200
Melting Completion (Liquidus), °C 220
1050
Melting Onset (Solidus), °C 220
880
Specific Heat Capacity, J/kg-K 220
370
Thermal Conductivity, W/m-K 60
62
Thermal Expansion, µm/m-K 22
18

Electrical Properties

Electrical Conductivity: Equal Volume, % IACS 12
13
Electrical Conductivity: Equal Weight (Specific), % IACS 15
13

Otherwise Unclassified Properties

Density, g/cm3 7.3
8.8
Embodied Carbon, kg CO2/kg material 16
3.3
Embodied Energy, MJ/kg 270
53

Common Calculations

Stiffness to Weight: Axial, points 3.8
7.0
Stiffness to Weight: Bending, points 17
18
Strength to Weight: Axial, points 1.1
8.3
Strength to Weight: Bending, points 2.9
10
Thermal Diffusivity, mm2/s 37
19
Thermal Shock Resistance, points 1.9
9.5

Alloy Composition


Deprecated: Automatic conversion of false to array is deprecated in /home/public/compare.php on line 460
Aluminum (Al), % 0 to 0.0010
0 to 0.0050
Antimony (Sb), % 0 to 0.1
0 to 0.2
Arsenic (As), % 0 to 0.030
0
Bismuth (Bi), % 0 to 0.1
0
Cadmium (Cd), % 0 to 0.0020
0
Copper (Cu), % 0.5 to 0.9
91 to 94
Gold (Au), % 0 to 0.050
0
Indium (In), % 0 to 0.1
0
Iron (Fe), % 0 to 0.020
0 to 0.2
Lead (Pb), % 0 to 0.070
0 to 0.3
Nickel (Ni), % 0 to 0.010
0 to 0.5
Phosphorus (P), % 0
0 to 0.050
Silicon (Si), % 0
0 to 0.0050
Silver (Ag), % 0.8 to 1.2
0
Sulfur (S), % 0
0 to 0.050
Tin (Sn), % 97.4 to 98.7
6.0 to 8.0
Zinc (Zn), % 0 to 0.0010
0 to 0.5
Residuals, % 0
0 to 0.6