Solder Alloy 715 vs. C99400 Brass

Solder alloy 715 belongs to the otherwise unclassified metals classification, while C99400 brass belongs to the copper alloys. There are 19 material properties with values for both materials. Properties with values for just one material (9, in this case) are not shown.

For each property being compared, the top bar is solder alloy 715 and the bottom bar is C99400 brass.

Metric UnitsUS Customary Units

Mechanical Properties

Elastic (Young's, Tensile) Modulus, GPa 51
120
Poisson's Ratio 0.36
0.34
Shear Modulus, GPa 19
44
Tensile Strength: Ultimate (UTS), MPa 30
460 to 550

Thermal Properties

Latent Heat of Fusion, J/g 61
230
Melting Completion (Liquidus), °C 220
1070
Melting Onset (Solidus), °C 220
1020
Specific Heat Capacity, J/kg-K 220
400
Thermal Expansion, µm/m-K 22
17

Electrical Properties

Electrical Conductivity: Equal Volume, % IACS 12
17
Electrical Conductivity: Equal Weight (Specific), % IACS 15
17

Otherwise Unclassified Properties

Density, g/cm3 7.3
8.7
Embodied Carbon, kg CO2/kg material 16
2.8
Embodied Energy, MJ/kg 270
45

Common Calculations

Stiffness to Weight: Axial, points 3.8
7.5
Stiffness to Weight: Bending, points 17
19
Strength to Weight: Axial, points 1.1
15 to 17
Strength to Weight: Bending, points 2.9
15 to 17
Thermal Shock Resistance, points 1.9
16 to 19

Alloy Composition


Deprecated: Automatic conversion of false to array is deprecated in /home/public/compare.php on line 460
Aluminum (Al), % 0 to 0.0010
0.5 to 2.0
Antimony (Sb), % 0 to 0.1
0
Arsenic (As), % 0 to 0.030
0
Bismuth (Bi), % 0 to 0.1
0
Cadmium (Cd), % 0 to 0.0020
0
Copper (Cu), % 0.5 to 0.9
83.5 to 96.5
Gold (Au), % 0 to 0.050
0
Indium (In), % 0 to 0.1
0
Iron (Fe), % 0 to 0.020
1.0 to 3.0
Lead (Pb), % 0 to 0.070
0 to 0.25
Manganese (Mn), % 0
0 to 0.5
Nickel (Ni), % 0 to 0.010
1.0 to 3.5
Silicon (Si), % 0
0.5 to 2.0
Silver (Ag), % 0.8 to 1.2
0
Tin (Sn), % 97.4 to 98.7
0
Zinc (Zn), % 0 to 0.0010
0.5 to 5.0
Residuals, % 0
0 to 0.3