Solder Alloy 716 vs. 50Cr-50Ni Alloy

Both solder alloy 716 and 50Cr-50Ni alloy are otherwise unclassified metals. Both are furnished in the as-fabricated (no temper or treatment) condition. There are 16 material properties with values for both materials. Properties with values for just one material (12, in this case) are not shown.

For each property being compared, the top bar is solder alloy 716 and the bottom bar is 50Cr-50Ni alloy.

Metric UnitsUS Customary Units

Mechanical Properties

Elastic (Young's, Tensile) Modulus, GPa 51
210
Elongation at Break, % 13
5.7
Poisson's Ratio 0.36
0.26
Shear Modulus, GPa 19
84
Tensile Strength: Ultimate (UTS), MPa 39
620

Thermal Properties

Latent Heat of Fusion, J/g 60
350
Specific Heat Capacity, J/kg-K 220
490
Thermal Expansion, µm/m-K 22
15

Otherwise Unclassified Properties

Density, g/cm3 7.3
8.0
Embodied Carbon, kg CO2/kg material 16
7.9
Embodied Energy, MJ/kg 270
110

Common Calculations

Stiffness to Weight: Axial, points 3.8
15
Stiffness to Weight: Bending, points 17
25
Strength to Weight: Axial, points 1.5
21
Strength to Weight: Bending, points 3.5
20
Thermal Shock Resistance, points 2.5
14

Alloy Composition

Aluminum (Al), % 0 to 0.0010
0 to 0.25
Antimony (Sb), % 0 to 0.1
0
Arsenic (As), % 0 to 0.030
0
Bismuth (Bi), % 0 to 0.1
0
Cadmium (Cd), % 0 to 0.0020
0
Carbon (C), % 0
0 to 0.1
Chromium (Cr), % 0
48 to 52
Copper (Cu), % 0.3 to 0.7
0
Gold (Au), % 0 to 0.050
0
Indium (In), % 0 to 0.1
0
Iron (Fe), % 0 to 0.020
0 to 1.0
Lead (Pb), % 0 to 0.070
0
Manganese (Mn), % 0
0 to 0.3
Nickel (Ni), % 0 to 0.010
44.5 to 52
Nitrogen (N), % 0
0 to 0.3
Phosphorus (P), % 0
0 to 0.020
Silicon (Si), % 0
0 to 1.0
Silver (Ag), % 0.8 to 1.2
0
Sulfur (S), % 0
0 to 0.020
Tin (Sn), % 97.6 to 98.9
0
Titanium (Ti), % 0
0 to 0.5
Zinc (Zn), % 0 to 0.0010
0